TY - JOUR ID - TI - Corrosion Behavior of V2AlC and Cr2AlC Compared with SS 316L in NaOH at Four Temperatures السلوك التآكلي للمواد V2AlC و Cr2AlC بالمقارنة مع الفولاذ المقاوم للصدأ في هيدروكسيد الصوديوم عند اربع درجات حرارية AU - Russul F. Faleh رسل فاضل فالح AU - Ahmed M. Al-Ghaban احمد محمد الغبان AU - Rana A. Anaee رنا عفيف عنائي PY - 2015 VL - 11 IS - 2 SP - 12 EP - 19 JO - Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية SN - 18181171 23120789 AB - This work involves the manufacturing of MAX phase materials include V2AlC and Cr2AlC using powder metallurgy as a new class of materials which characterized by regular crystals in lattice. Corrosion behavior of these materials was investigated by Potentiostat to estimate corrosion resistance and compared with the most resistant material represented by SS 316L. The experiments were carried out in 0.01N of NaOH solution at four temperatures in the range of 30–60oC. Polarization resistance values which calculated by Stern-Geary equation indicated that the MAX phase materials more resistant than SS 316L. Also cyclic polarization tests confirmed the resistivity of MAX phase materials through disappears of hysteresis loop.

يتضمن هذا البحث تصنيع مواد الطور MAX التي تُعد من المواد الجديدة المميزة بانتظام في الشبكة البلورية باستخدام ميتالورجيا المساحيق، وتم دراسة السلوك التآكلي لهذه المواد باستخدام المجهاد الساكن لتقدير متغيرات التأكل والمقارنة مع المادة الاكثر مقاومة والممثلة بالفولاذ المقاوم للصدأ 316L. اجريتْ جميع التجارب في وسط قاعدي من هيدروكسيد الصوديوم بتركيز 0.01 نورمالية وعند اربع درجات حرارية ضمن المدى 30 – 60 درجة مئوية. وقد بينتْ نتائج مقاومة الاستقطاب المحسوبة بمعاولة ستيرن-جيري بان المواد المحضرة تمتلك مقاومة افضل من الفولاذ المقاوم للصدأ. كما ان الاستقطاب الحلقي اكد مقاومية هذه المواد مقارنة مع الفولاذ المقاوم للصدأ من خلال عدم ظهور الحلقة الهستيرية. ER -