TY - JOUR ID - TI - Corrosion and Structure Characterization of Anodized Ti- 6Al-7Nb Alloy خصائص التركيب والتآكل لسبيكة Ti-6Al-7Nb المؤنونه AU - Thair L. Alzubaydi AU - Mustafa Sh. AlHilfi PY - 2014 VL - 32 IS - 3 Part (B) Scientific SP - 568 EP - 583 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - Electrochemical and structural properties of titanium implant materials with a nanotube surface treatment and heat treatment were examined. Amorphous TiO2 nanotubes were grown homogeneously on α phase of Ti-6Al-7Nb alloy. Amorphous TiO2 nanotubes were partially crystallized to rutile by heat treatment at 8000C for 2 hrs. The corrosion potential (Ecorr) of the annealed sample had value of -162.881mV due to the stable TiO2 crystal phase compared to the -343.629 mV observed in the untreated sample. At 0.5 V, where a passive layer had formed, the corrosion resistance of the annealed sample was approximately ten times that of the untreated sample.

فحصت الخواص التركيبية والكهروكيميائية لزروعات التيتانيوم بعد تكوين انابيب نانوية على سطحها ومعالجتها حراريا.تكونت انابيب نانويه ذات تركيب عشوائي من ال TiO2بصورة منتظمه على طورα لسبيكة Ti-6Al-7Nb .هذه الانابيب النانوية تبلورت جزئيا الى طور Rutile بعد التسخين الحراري بدرجة 8000C لساعتين.جهد التاكل للنموذج الملدن هو-162.881mV بسبب الطور البلوري المستقر ل TiO2بينما كان هذا الجهد للنموذج الغير معامل -343.629 mV . عند 0.5 V حيث تكونت الطبقة المانعه للتاكل فان مقاومة التاكل للنموذج الملدن كانت اكبر بعشرة مرات من تلك للنموذج غير المعامل. ER -