TY - JOUR ID - TI - Nanostructure Cadmium Oxide Thin Film Prepared by Vacuum Evaporation Thermal Technique اغشية اوكسيد الكادميوم ذات التركيب النانوي المحضرة بتقنية التبخيرالحراري بالفراغ AU - Wafaa K.Khale PY - 2014 VL - 32 IS - 5 Part (B) Scientific SP - 1009 EP - 1018 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - Cadmium Oxide films have been prepared by vacuum evaporation technique on a glass substrate at room temperature. Structural optical and morphological properties of the films are studied at different oxidation temperatures (573 To 773) K, for the thickness (300) nm at 30 mint. XRD pattern confirm the films shows the polycrystalline nature of the film with preferential orientation along (111) plane. The film deposited with higher oxidation temperatures shows higher transmittance compared to others. Direct energy band gap of CdO thin film increases with increases of oxidation temperature. From AFM measurement, the average grain size is in the range of nanometer and it shows the faceted columnar microstructure of the film is perpendicular to the surface.

تم تحضير اغشية اوكسيد الكادميوم بواسطة بواسطة تقنية التبخير بالفراغ على قواعد زجاجية بدرجة حرارة الغرفة .الخصائص التركيبية ,البصرية والسطحية للاغشية المحضرة شخصت بدرجات حراريه مختلفة ( 573الى 773 ) كلفن عند سمك غشاء (300) نانوميتر . تقنية حيود الاشعة السينية شخصت اغشية اوكسيد الكادميوم بمتعدد البلورات وذو اتجاهية مفضلة ( 111). لقد وجد ان الاغشية الموكسدة عند درجات حرارةعالية تمتلك اعلى نفاذية ,اضافة الى ذلك قيمة فجوة الطاقة تزداد مع زيادة درجة حرارة الاكسدة .من خلال قياس مجهر القوه الذري وجد ان ابعاد جسيمات الغشاء بالنانوميترو ذات بنية الاعمدة المايكروية العمودية على سطح الغشاء . ER -