TY - JOUR ID - TI - Laser Peening on Aluminum Alloy 7049 Using Black Paint Surface Coating الصفع الليزري لسبيكة الالمنيوم 7049 باستخدام الطلاء الاسود للسطوح AU - Alalkawi H. J. M. حسين جاسم العلكاوي AU - Basim A. Sadkhan باسم عاجل سدخان AU - Noor N. Abed نور نجم عبد PY - 2015 VL - 11 IS - 3 SP - 54 EP - 60 JO - Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية SN - 18181171 23120789 AB - Black paint laser peening (bPLP) technique is currently applied for many engineering materials , especially for aluminum alloys due to high improvement in fatigue life and strength . Constant and variable bending fatigue tests have been performed at RT and stress ratio R= -1 . The results of the present work observed that the significance of the surface work hardening which generated high negative residual stresses in bPLP specimens .The fatigue life improvement factor (FLIF) for bPLP constant fatigue behavior was from 2.543 to 3.3 compared to untreated fatigue and the increase in fatigue strength at 107 cycle was 21% . The bPLP cumulative fatigue life behavior was improved by 1.786 at L-H and 1.55 at H-L due to black paint coating .

ان تقنية التصليد بالليزر مع استخدام الصبغ الاسود تستخدم لكثير من المواد الهندسية ولاسيما سبائك الالمنيوم بسبب انها تعمل على تحسين اعمار ومقاومة الكلال . تم انجاز فحوصات الكلال الانحنائيه ثابتة ومتغيرة السعة عند درجة حرارة الغرفة ونسبة اجهاد (R=-1 ) . نتائج هذا العمل لوحظ اهمية عمل التصليد السطحي نتيجة الاجهادات الضغطية المتبقية المتولدة من العينات المطلية بالصبغ الاسود . عامل تحسين عمر الكلال ثابت السعة (FLIF) للعينات المطلية بالصبغ الاسود كانت من 2.543 الى 3.3 مقارنة مع الكلال غير المعالج وعملية الطلاء بالصبغ الاسود والليزر ادت الى زيادة في مقاومة الكلال عند 107 دورة بنسبة 21% . اما سلوك اعمار الكلال التراكمي ( متغيرة السعة ) فان التصليد بالليزر مع الطلاء بالصبغ الاسود ادت الى تحسن في الاعمار بمقدار 1.786 عند الاجهادات من واطئة (L ) الى عالية (H ) و 1.55 من الاجهادات العالية الى الواطئة نتيجة التصليد بالليزر مع الطلاء بالصبغ الاسود . ER -