TY - JOUR ID - TI - Studying of Some Mechanical Properties of Reactive Powder Concrete Using Local Materials دراسة بعض الخواص الميكانيكية لخرسانة المساحيق الفعالة باستخدم مواد محلية AU - Mohammed Mansour Kadhum محمد منصور كاظم PY - 2015 VL - 21 IS - 7 SP - 113 EP - 135 JO - Journal of Engineering مجلة الهندسة SN - 17264073 25203339 AB - This research aims to investigate and evaluate a reactive powder concrete (RPC) cast using economical materials. Its mechanical properties were investigated and evaluated by studying the effects of using different cement and silica fume contents and locally steel fibers aspect ratios as reinforcement for this concrete. A compressive strength of about 155.2MPa, indirect tensile strength of 16.0MPa, modulus of elasticity of 48.7GPa, flexural strength of 43.5MPa, impact energy of 3294.4kN.m and abrasion loss 0.59% have been achieved for reinforced RPC contains 910 kg/m3 cement content, silica fume content 185 kg/m3 of cement weight and fiber volume fraction 2%. The water absorption values were 1.5 times higher for the normal strength concrete in comparison with the reactive powder concrete.

يهدف هذا البحث لتحري وتقييم خرسانة المساحيق الفعالة المصنوعة من استخدام مواد اقتصادية. تم دراسة وتقييم خواصها الميكانيكية باستخدام انواع مختلفة من السمنت وغبار السيلكا والياف الحديد المحلية الصنع. من النتائج العملية المستحصلة لوحظ بان مقاومة الانضغط للخرسانة كانت 155,2 ميكاباسكال، 16,0 ميكاباسكال مقاومة الشد الغير مباشرة، 48,7 ميكاباسكال معامل المرونة الاستاتيكي، 43,5 ميكاباسكال لمقاومة الانثناء، 3294,4 كن.م و 0.59% فقدان الاحتكاك وهذه القيم تحققت لخرسانة المساحيق الفعالة المسلحة بالالياف بنسة حجمية 2% والحاوية على سمنت 910 كغم/م3 ومحتوى السيلكا 185 كغم/م3 من وزن السمنت. اما مقدار الامتصاص فقد سجل من الشغل العملي 1.5 مرة اكثر للخرسانة الاعتيادية مقارنة بخرسانة المساحيق الفعالة. ER -