@Article{, title={Swelling Behavior of Cross-link PVA with Glutaraldehyde سلوك الانتفاخ للبولي فاينيل الكحول المتشابك عرضيا مع الكلوتارالديھايد}, author={Fadhel S. Matty فاضل سليم متي and Maha T. Sultan مها طاهر سلطان and Adiba Kh. Amine أديبة خيون أمين}, journal={Ibn Al-Haitham Journal For Pure and Applied Sciences مجلة ابن الهيثم للعلوم الصرفة والتطبيقية}, volume={28}, number={2}, pages={136-146}, year={2015}, abstract={The polymeric hydrogels composed of poly vinyl alcohol (m.wt 72000) andglutaraldehyde(5%,8% and 10%) , have been thermally prepared for the purpose of studyingtheir swelling and drug release behavior .The swelling ratio was measured for all the hydrogel samples at 37°C, in three differentmedia pH (1.2, 4.7 and 6.8) as a function of time. The results show that the maximumswelling ratios were arranged as follows :pH =6.8 > pH =4.7 > pH =1.2 hydrogels crosslinked PVA showed a typical pH responsive behavior such as high pH has maximumswelling while low pH shows minimum swelling

الانتفاخ.النماذج المحضرة تختلف بالعوامل المستعملة في التشابك ونسب التشابك كألاتي .PVA (M.wt 72000) +GA, 5% , 8% and 10%)اذ اثبتت FTIR الخطي تم تشخيصه بوساطة طيف PVA المتشابك الھلامي وال PVA ان التركيب الكيميائي لوالمجاميع الفعالة لعوامل التشابك. PVA النتائج تكون تشابكات بين مجاميع الھيدروكسيل ل( التي ھي , 1.2 pH 37 في ثلاثة اوساط مختلفة ال °C وقد تم قياس نسب الانتفاخ لجميع نماذج الھلامية عند درجة4.7 كدالة للزمن. , 6.8 )لمحاليل بفر. pH المتشابكة تعتمد على قيمة PVA وتم ملاحظة ان درجة الانتفاخ لھلامياتفي نسب الانتفاخ لجميع التراكيب الھلامية ووجد من النتائج ان اعلى نسبة انتفاخ كانت حسب pH وتم دراسة تأثير قيمةالترتيب الاتي .pH = 6.8 > pH =4.7 > pH= 1.2} }