TY - JOUR ID - TI - Some Durability Test of No-Fine Concrete بعض فحوصات ديمومة الخرسانه الخاليه من الركام الناعم AU - Shakir Ahmed Salih شاكر أحمد صالح AU - Tuqa Alaa Fidel تقى علاء فاضل PY - 2016 VL - 22 IS - 1 SP - 15 EP - 30 JO - Journal of Engineering مجلة الهندسة SN - 17264073 25203339 AB - In this study, two types of mixes were adopted by using two grading of coarse aggregate. The practical side of this study was to produce no-fine aggregate concrete by using crushed clay brick aggregates. The durability of the produced concrete and internal sulfate attack was studied. For durability assessment, it is found that the no-fine concrete made with crushed brick aggregate lost about (15-25) % of its compressive strength after being subjected to 60 cycles of wetting and drying with age 120 days. The curing condition showed that the water curing improved the compressive strength with a rate higher than that when sealed or air dry curing were used. The crushed brick no-fine concrete deteriorated in compressive strength after exposure to internal sulfate attack for 60 cycles; the percentage decrease was about (23.33-25) and (25-27.5) % for 0.57 and 0.83sulfate content respectively.

تم خلال هذه الدراسه استخدام نوعين من الخلطات الخرسانيه الخفيفه الوزن حاويه على تدرجين من الركام الخشن. تضمن الجانب العملي من البحث انتاج خرسانه خاليه من الركام الناعم باستخدام الركام الاعتيادي ومكسر الطابوق. وتم دراسة ديمومة الخرسانه الخفيفه في البحث. لتقيم الديمومه وجد ان مقاومه الانضغاط للخرسانه الخاليه من الركام الناعم تنخفض من (15-25) % بعد تعرضها الى 60 دورة ترطيب وتجفيف بعمر يعادل 120 يوم. كما وجد ان مقاومه لانضغاط عند انضاج النماذج في الماء افضل مقارنا مع انضاجها في الهواء الجاف او المغلفه باستخدام النايلون. كما دلت النتائج على تدهور الخرسانه الخاليه من الركام الناعم بعد تعرضها الى 60 دوره ترطيب وتجفيف كما وجد ان معدل النقصان في مقاومه الانضغاط يصل الى (25-27.5) % عندما يكون محتوى الاملاح 0.57 و 0.83 على التوالي. ER -