TY - JOUR ID - TI - Characterization of CuO thin films for gas sensing applications وصف أغشية اوكسيد النحاس الرقيقة لتطبيقات التحسس الغازي AU - Jamal M. Rzaij جمال مال لله رزيج PY - 2016 VL - 14 IS - 31 SP - 1 EP - 12 JO - Iraqi Journal of Physics المجلة العراقية للفيزياء SN - 20704003 26645548 AB - Nanostructural cupric oxide (CuO) films were prepared on Si and glass substrate by pulsed laser deposition technique (PLD) using laser Nd:YAG, using different laser pulses energies from 200 to 600 mJ. The X-ray diffraction pattern (XRD) of the films showed a polycrystalline structure with a monoclinic symmetry and preferred orientation toward (111) plane with nano structure. The crystallite size was increasing with increasing of laser pulse energy. Optical properties was characterized by using UV–vis spectrometer in the wave lengthrange (200-1100) nm at room temperature. The results showed that the transmission spectrum decreases with the laser pulses energy increase. Sensitivity of NO2 gas at different operating temperatures, (50°C, 100°C, 150°C and 200°C) was calculated.

تحضير اغشية اوكسيد النحاس النانوية على ارضيات من الزجاج والسليكون باستخدام تقنية الترسيب بالليزرالنبضي باستخدام ليزر النيدميوم –ياك باستخدام طاقات نبضة ليزر مختلفة من 200 الى 600 ملي جول. ان نمطحيود الاشعة السينية اظهرت أن الأغشية تمتلك تركيب متعدد البلورات ذات تناظر من النوع احادي الميلبدورانية ( 111 ) وذات تركيب نانوي. كانت هناك زيادة في الحجم الحبيبي مع زيادة طاقة نبضة الليزر. تم تمييزالخصائص البصرية باستخدام مطياف الاشعة فوق البنفسجية-المرئية ضمن مدى الطول الموجي ( 200 الى1100 نانومتر) بدرجة حرارة الغرفة، أظهرت النتائج ان طيف النفاذية يقل مع زيادة طاقة نبضة الليزر. تمعند درجات حرارية مختلفة ( 50 °م، 100 °م، 150 °م و (NO حساب التحسسية لغاز ثاني اوكسيد النتروجين ( 2° 200 م). ER -