TY - JOUR ID - TI - Preparation of Calcium Phosphate Via Precipitation Technique تحضير فوسفات الكالسيوم بتقنية الترسيب AU - Wafaa A. Hussain AU - Luay H. Alwan PY - 2015 VL - 33 IS - 8 Part (B) Scientific SP - 1412 EP - 1419 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - Recently, there has been an increasing attention on the preparation of calcium phosphates CaP for the development, understanding and manufacturing of biomaterials. In this study, precipitation process was performed to prepare calcium phosphates powders by varying the Ca/P molar ratio as (1.54, 1.67 and 1.8). Calcium acetate was added to disodium hydrogen phosphate, the precipitate was left overnight and dried at 100oC and then the powder was treated at 900oC for 1 hour. The powder sample was evaluated using such as scanning electron microscope (SEM), X-ray diffraction (XRD), atomic force molecules (AFM) and Fourier Transform Infrared (FTIR). It can be concluded, it is possible to synthesis hydroxyapatite (HA) and biphasic calcium phosphate (BCP) powders with nano particle.

ازداد الاهتمام في الوقت الحاضر في تحضير فوسفات الكالسيوم لتطوير و فهم وصناعة المواد الحيوية. في هذه الدراسة تم تنفيذ عملية الترسيب لتحضير مساحيق فوسفات الكالسيوم وذلك بتغيير النسبة المولارية للكالسيوم الى الفوسفات (1.54 و 1.67 و1.8 ). تم إضافة اسيتات الكالسيوم إلى فوسفات هيدروجين ثنائي الصوديوم, ترك الراسب ليلة كاملة وجفف عند 100 oم وبعدها تم معاملة المسحوق عند 900 oم لمدة ساعة. قيمت عينة المسحوق باستخدام المجهر الالكتروني الماسح و حيود الأشعة السينية وجزيئات القوة الذرية و مطيافية الاشعة تحت الحمراء. يمكن الاستنتاج انه من الممكن تصنيع مساحيق هايدروكسيابتايت وفوسفات الكالسيوم ثنائي الطور بجسيمات نانويه. ER -