@Article{, title={INVESTIGATION OF FATIGUE BEHAVIOR USING SURFACE SHOT PEENED TECHNIQUE FOR 2024 – T4 AL-ALLOY 2024-T4دراسة تصرف الكلال باستخدام تقنية القذف بالكريات لسبيكة الالمنيوم}, author={Hussain J. M. Alalkawi Rawaa Hamid Al-Kalali Shatha M.R. Abdul Jabbar حسين جاسم العلكاوي رواء حامد محمد شذى محمد رجاء عبدالجبار}, journal={Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد}, volume={16}, number={2}, pages={129-142}, year={2016}, abstract={The strength and fatigue lifetime of AL alloy 2024-T4 were estimated using flat fatigue specimen and stress ratio R=-1 at room temperature (RT). After fatigue testing,it was found that both fatigue region (low cycle fatigue and high cycle fatigue) was improved after the shoot penning of the surface .This improvement appeared due to the compressive residual stress established at the shoot penned surface . Also, the fatigue life improvement factor was obtained around (6) while the fatigue strength factor was found to be around 26.

تم تقيم مقاومة وعمر الكلال لسبيكة الألمنيوم2024-T4 باستخدام عينات الكلال المسطحة ونسبة إجهاد R= -1 عند درجة حرارة الغرفة باستخدام تقنية القذف بالكريات لعشرة دقائق . بعد الفحص تبين ان أداء الكلال لهذه السبيكة المشار اليها أعلاه لكلا منطقتي الكلال واطئ الدورات وعالي الدورات قد تحسن . ظهر هذا التحسن ربما لخلق اجهادات ضغطية متبقية على السطح . اعمار الكلال ازدادت بعامل تحسن الأعمار بمقدار 6 بينما عامل مقاومة الكلال النسبي (FSF%) وجد انه حوالي 26.} }