TY - JOUR ID - TI - FABRICATION POROUS COPPER BY SINTERING’S TECHNIQUE UNDER VACUUM CONDITIONS انتاج نحاس مسامي باستخدام تقنية التلبيد في أجواء مفرغة AU - Salah N. Alnomani1 and Abdalwahid K. Rajih2 د.عبدالواحد كاظم راجح صلاح نوري النعماني PY - 2016 VL - 16 IS - 3 SP - 285 EP - 296 JO - Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد SN - 20761819 AB - In this study, porous copper was produced using powder metallurgical techniques. Zinc element (21%wt) was used as a transitional element to be pulled during sintering process under vacuum environment. A set of samples was produced with different sintering’s conditions to investigate the optimal parameters for production of porous copper. SEM test was used to measure the resulted porosity for the prepared samples. It was found that 3 hours is a sufficient duration for the first stage of sintering at (350oC) and for the second stages at (850oC) to pull all of the zinc vapors and thus get the highest percentage of porosity for the remaining copper which was found to be (19%).

في هذه الدراسة، تم إنتاج النحاس المسامي باستخدام تكنولوجيا المساحيق. وقد استخدم عنصر الزنك بنسبة وزنية (21%wt) كعنصر انتقالي ليتم سحبه بعد ذلك خلال عملية التلبيد في ظل أجواء مفرغة. تم انتاج مجموعة من العينات تحت ظروف تلبيد مختلفة لغرض استقصاء تلك الظروف التي تحقق أفضل المعايير في انتاج النحاس المسامي. تم استخدام المجهر الألكتروني لغرض قياس المسامية للعينات المعدة. وقد وجد أن التلبيد لمدة ثلاث ساعات خلال المرحلة الأولى بدرجة حرارة (350oC) و للمرحلة الثانية بدرجة حرارة (850oC) للتلبيد ينتج عنه تبخر محتوى الزنك بشكل شبه كامل وبالتالي الحصول على أعلى نسبة من المسامية للنحاس المتبقي بلغت قيمتها (19%) . ER -