@Article{, title={Study the structural and Optical properties of ZnO thin film دراسة الخواص التركيبية والبصـرية لاغشية أوكسيد الخارصين الرقيقة}, author={Abdul Majeed E.Ibrahim1 عبد المجيد عيادة إبراهيم1 and Raid A. Isma'el2 رائد عبد الوهاب إسماعيل2 and Enad S.Ibrahim1 عناد صالح إبراهيم1 and Essam M.Ibrahim3 عصام محمد إبراهيم3}, journal={Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة}, volume={22}, number={1}, pages={148-155}, year={2017}, abstract={This research included preparation of ZnO thin films from Zinc acetate solution (Zn(CH3COO)22H2O). on glass substrate with dimension (2.5cmx2.5cmx0.1cm) using chemical spray pyrolysis method composed with (0.2M). The structural properties were characterized by X-Ray diffraction (XRD), Atomic force microscope (AFM), Scanning electron microscope (SEM) and Energy dispersive of X-Ray (EDX). The film grown have a polycrystalline wurtizte structure it can be seen that the highest texture coefficient was in (002) plane. So (AFM) measurement show that the roughness average (1.51nm), root mean square (RMS = 1.75nm) and dimeter average (108.96nm). The optical properties were characterized by (UV- Visible) and showed that higher transmittance about (97%) and optical Energy gab (Eg=3.28 eV).

تضمن البحث تحضير اغشية ZnO الرقيقة من محلول اسيتات الخارصين (Zn(CH3COO)22H2O) على قواعد زجاجية بابعاد (2.5x2.5x0.1 cm) بطريقة الرش الكيميائي الحراري، وبتركيز (0.2 M)، ودراسة خواصها التركيبية من خلال حيود الاشعة السينية (XRD) ومجهر القوة الذرية (AFM) والمجهر الالكتروني الماسح (SEM)، وتفريق الطاقات باستخدام الاشعة السينية (EDX)، والتي أظهرت ان الاغشية متعددة التبلور (Polycrystalline )، وذات تركيب سدادسي متراص (wurtzite) والاتجاه البلوري السائد (002)، وبين فحص (AFM) ان معدل خشونة الغشاء (1.51 nm)، وبمعدل قطر (108.96 nm)، و (1.75 nm=RMS )، ودراسة الخواص البصرية للغشاء باستخدام مطياف (UV visible) للاطوال الموجية من (200 nm – 1200 nm) فكانت فجوة الطاقة (Eg=3.28 ev) والنفاذية (T=97%).} }