@Article{, title={Effect of decomposition temperature on crystallite size and strain for alumina تأثير التفكك الحراري على المقاس الحبيبي والانفعال للألو مينا Al2O3}, author={Ghazi K.Saeed غازي كمال سعيد and Sattar A.Abass ستار عبود عباس}, journal={Univesity of Thi-Qar Journal مجلة جامعة ذي قار العلمية}, volume={10}, number={1}, pages={1-8}, year={2015}, abstract={The crystallite size and strain of Al2O3 ceramic powder have been determined from x-ray line-broadening analysis at different decomposition temperatures. The Al2O3 powder have been prepared from decomposition of aluminum hydroxide Al(OH)3 at different temperature which have been characterized by X-Ray diffraction (XRD) and Differential, Thermal Analysis (DTA) methods. Deconvolution of the experimental profiles by Fourier cosine coefficients has resulted in corrected values of crystallite size. The crystallite size has been found to increase with increasing decomposition temperature from 38nm at 1673k to 73nm at 1873k. Strain on the other hand decrease from 3.04×10-3 at 1673k to 1.14×10-3 at 1873k. Estimation of micro hardness on compacts of different crystallite size has shown that crystallite size may influence the bearing load that compact can endure

تم تحديد الحجم الحبيبي والانفعال لمسحوق الالومينا بواسطة تحليل الاتساع في خط حيود الأشعة السينية عند درجات حرارة مختلفة . حضر مسحوق الالومينا من التفكك الحراري لهيدروكسيد الألمنيوم Al(OH)3 عند درجات حرارة مختلفة والذي شخص بواسطة جهازي حيود الأشعة السينية وجهاز التحليل الحراري التفاضلي . درست قيم المقاس البلوري بأخذ جذر متوسط مربع الانفعال بواسطة تحليل الاتساع في خط حيود الأشعة السينية باستخدام طريقة فورير. وجد إن المقاس البلوري يزداد بزيادة التفكك الحراري من 38 نانومتر عند درجة حرارة1673 كلفن إلى 73 نانومتر عند 1873 كلفن . من جانب أخر الانفعال يقل من 3-10x3.04 عند 1673 كلفن إلى 3-10x1.14عند 1873 كلفن. يعطي المسحوق المكبوس للالومينا صلادة مجهريه تزداد كلما قل الحجم الحبيبي .} }