TY - JOUR ID - TI - The Effect of Precipitation Hardening on Micro structural Welded Joint of Aluminum Alloy (2024T3) تأثير التصليد بالترسيب على البنية المجهرية لوصلات لحام سبيكة الألمنيوم (2024T3) AU - فاضل عباس هاشم AU - عبد الله عذيب مشاري AU - عبد الكريم سعدون محسن PY - 2014 VL - 5 IS - 2 SP - 1 EP - 14 JO - University of Thi-Qar Journal for Engineering Sciences مجلة جامعة ذي قار للعلوم الهندسية SN - 26645564 26645572 AB - The aim of this work is to study the possibility of joining the Aluminum alloy (2024T3) by the Manual Metal Arc Welding (MMAW) using the (E4043) electrode, and studying the microscopic structure in the joint area.A )V-Butt joint) were prepared before and after the heat treatment then thermally treated after welding (Solution treating and aging). It was clear that the molten zone (Fusion Zone) will be containing epitaxial growth, also it contains the phase (Al2Cu) what it called copper-rich phase, that was in case of not using heat treatment, but when using heat treatment before welding, the copper-rich phase will be less and the heat treatment after welding will result in distortion of that phase.

يهدف البحث إلى دراسـة أمكانيـة ربط سبيكـة الألمنيوم (2024T3) بطريقـة لحـام القوس الكهربائي اليدوي (MMAW ) (Manual Metal Arc Welding) وباستخدام قضيب لحام نوع (E4043) ودراسة البنية المجهرية في منطقة الربط حيث تم تهيأت وصلات لحام تناكبية (V-Butt joint) قبل وبعد المعاملة الحرارية ومعاملتها معاملة محلوليه ثم تتبع بالتعتيق بعد اللحام (Solution treating and aging) وتبين أن المنطقة المنصهرة (Fusion Zone) تكون محتوية على شجيرات طولية (Epitaxial growth) ومحتوية على الطور (Al2Cu) ما يسمى بالطور الغني بالنحاس (Copper-rich phase) هذا في حالة اللحام بدون معاملة حرارية ، أما عند إجراء معاملة حرارية قبل اللحام فأن الطور الغني بالنحاس يكون أقل والمعاملة الحرارية بعد اللحام تؤدي إلى تشتيت ذلك الطور. ER -