@Article{, title={CORROSION BEHAVIOR AND ROUGHNESS OF NI-CR/AL2O3 COMPOSITES AS DENTAL RESTORATIVE السلوك التآكلي والخشونة لمتراكبات Ni-Cr/Al2O3 كمواد تعويضية في الاسنان}, author={Rana Afif Anaee* Hiba Anwer Abdulah* Shamaa Hadi Jawad** Mahamed Mahdy Jabar* رنا عفيف* هبة انور عبدالله * شيماء هادي جواد** محمد مهدي جبار*}, journal={Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد}, volume={17}, number={1}, pages={159-169}, year={2017}, abstract={This work investigated on the corrosion behavior and roughness of Ni-Cr alloy as dental restorative. Alumina with three weight percentages (1, 5 and 10%) added as reinforcement to fabricate Ni-Cr/alumina composites. Corrosion behavior was tested in artificial saliva at 37+1 oC and pH=4.4. The data of corrosion indicated that the addition of alumina led to reduce the dissolution of metals in base alloy due to the enhancing of Cr2O3 passive film and producing Ni3Al phase in matrix. The roughness of surface was reduced for composites compared with base alloy (Ni-Cr) which is important factor to reduce the accumulation of bacteria on restorative materials in mouth; this reduction is due to the formation of ductile Ni3Al compared with brittle Ni2Cr3 in composites.

يتضمن البحث الحالي التقصي عن السلوك التآكلي والخشونة لسبيكة نيكل – كروم، كما اضيقت الالومينا بثلاث نسب وزنية 1 و5 و 10% كتقوية للسبيكة الاساس. اجري فحص التآكل في محلول اللعاب الصناعي عند اس هيدروجيني 4.4 ودرجة حرارة 37+1 درجة مئوية وقد اظهرت النتائج بان اضافة الالومينا يؤدي الى تقليل الذوبان المعدني للسبيكة الاساس بسبب تعزيز طبقة اوكسيد الكروم الحامية وتكوين الطور Ni3Al. كما بينتْ نتائج فحص الخشونة السطحية بان المواد المتراكبة تمتلك خشونة اقل من السبيكة الاساس وهذا ما يعد عامل اساسي لتقليل تجمع البكتريا على المواد التعويضية المستخدمة داخل الفم. ان النقصان الحاصل في الخشونة سببه تكوين Ni3Al اللدن مقارنة مع الطور Ni2Cr3 الهش.} }