TY - JOUR ID - TI - abrication Compound Sn2-xAgxBa2Ca2Cu3O10+& Superconductor and Study the Nano and Electrical Propertes تحضير مركب Sn2-xAgxBa2Ca2Cu3O10+& مفرط التوصيل ودراسة خواصه النانوية والكهربائية AU - Nihad Ali Shafeek نهاد علي شفيق PY - 2017 VL - 12 IS - 1 SP - 334 EP - 350 JO - Kirkuk Journal of Science مجلة كركوك للعلوم SN - 30054788 30054796 AB - The two step Solid-State method used to prepared a whole range materials including mixed metal oxides and nitrides in different concentrations (x = 0.1, 0.2, 0.3, and 0.4). samples were then subjected to Nano technique under hydrolic pressure 8 ton/cm2 samples have been sintrig in (850 0C ). The resultes show that Samples morphology were observed by AFM (in three dimensions), the best value of Nano is 88.61 nm at x= 0.2. . Electrical resistivity at x = 0.2 of Ag are obtained when the best value of Tc= 140 K.

تم تحضير عينات المركب Sn1-xAgxBa2Ca2Cu3O10+& بطريقة تفاعل الحالة الصلبة بمرحلتين باخذ اوزان اكاسيد ونترات العناصر وبنسب تعويض مختلف ( x= 0.1,0.2,0.3, and 0.4 ) كبست العينات تحت ضغط 0.85 Gpa اجريت عملية تلبيد تحت درجة حرارة 875 0C لمدة 48 ساعة وتم اعادة كبس وتلبيد العينات تحت نفس الظروف , واجريت عملية فحص العينات باستخدام جهاز AFM الليزري لفحص الابعاد النانوية والصور الفوتوغرافية , استخدمت جهازFour-Probe لقياس مقاومية النماذج بعد معرفة التيار والفولتية وابعاد النماذج لوحظ من خلال النتائج ان افضل درجة حرارة حرجة هي Tc = 140 K عند بعد نانوي 88.64 nm وذلك عند نسبة التعويض x = 0.2 وهذا يدل على ان افضل نسبة تعويض هي x =0.2 للفضة . ER -