@Article{, title={Effective ZnO Doping by pulsed laser deposition to Improve the efficiency of the solar cells of TiO2at 200 C0 تأثير تطعيم اوكسيد الخارصين بواسطة ترسيب الليزر النبضي لتحسين كفاءة الخلية الشمسية للأوكسيد التياتيوم عند درجة حرارة (200) C0}, author={Batool Gabbar Obeid}, journal={journal of kerbala university مجلة جامعة كربلاء}, volume={15}, number={3}, pages={63-68}, year={2017}, abstract={In this research was prepare TiO2: ZnO have been deposited on the glass substrates by the pulsed lasertechnique,the use of Nd:YAG laser with wavelength (1064)nm and energy 600mJand have been deposited with different concentration(0.03,0.05,0.07,0.1)% of ZnO at annealing temperature 200 C0with thickness (400 nm). The TiO2thin films showed n-type conductivity, according to Hall measurements, the carrier concentration of TiO2 thin films had increasedfrom (18.5× 1010 to 45.16× 1010 cm−3). The average absorbance value of TiO2 thin films was improved from (3.412*10-6to 8.654*10-6)by the doping of ZnO., These improved properties should contribute to the efficiency of the photovoltaic effect of the photogenerated charged carriers. The( I-V) characteristic of (Al / TiO2: ZnO /n-Si / Al) heterojunction show that the solar cell which is produced at X=0.1% by efficiency (η) =8.769

تم تحضير اغشية اوكسيد التياتيوم على قواعد من الزجاج باستخدام تقنية الترسيب بالليزر النبضي حيث تم استخدام ليزر النديميوم- ياك النبضي ذو الطول الموجي(1064nm)وبطاقة (600 mj)ومن ثم تم ترسيب هذه الاغشيةبأوكسيد الخارصين بتراكيز مختلفة(0.03 , 0.05 , 0.07 , 0.1)% وبدرجة حرارة ) 200 C0)وبسمك (400nm ).وبينت قياسات هول ان الاغشية المحضرة تكون ذات توصيلية سالبة حيث نلاحظ كلما زداد نسبة التراكيز تزداد تراكيز الحاملات من(18.5× 1010) الى(45.16× 1010 cm−3) وكذلك تزداد التوصيليةمن 3.412*10-61/Ω.cm)الى 8.654*10-6)وهذه الخصائص ساهمت في تحسين كفاءة الخلية الشمسية بينت خواص تيار- فولتية للمفرق الهجين (Al / TiO2: ZnO /n-Si / Al) الحصول على خلية شمسية حيث عند التركيز%0.1ذات كفاءةعاليه8.769} }