@Article{, title={Development the Mechanical Properties of (AL-Li-Cu) Alloy تطوير الخواص الميكانيكية لسبيكة ألمُنيوم– ليثيوم– نحاس}, author={Awatif Mustafa Ali عواطف مصطفى علي and Ihsan Kadhom AlNaimi إحسان كاظم عباس النعيمي}, journal={Journal of Engineering مجلة الهندسة}, volume={23}, number={11}, pages={43-55}, year={2017}, abstract={The aim of this research is to develop mechanical properties of a new alloy aluminum-lithium-copper which is prepared by casting under control atmosphere in a permanent metal mold. The mechanical properties (impact, elasticity modulus, tensile strength, and fatigue) with microstructure were examined before and after heat treatment. The research outcome showed that the modulus of elasticity of the prepared alloy is higher than standard alloy about 2%. While the alloy that was heat treated for 6 h and cooled in water, showed a higher ultimate tensile stress comparing with as-cast alloy. The homogenous heat treatment gives best fatigue behavior compared with as-cast and other heat treatment alloys. Also, the impact test illustrates that the homogeneous heat treatment alloy gives the highest value.

الهدف من هذا البحث هو تطوير الخواص الميكانيكية لسبيكة جديدة من ألمُنيوم- ليثيوم- نحاس. هذه السبيكة حضرت بطريقة السباكة بقالب معدني دائمي تحت ظروف جوية مسيطر عليها. تم فحص التركيب المجهري وأجريت الفحوصات الميكانيكية للسبيكة قبل وبعد المعاملة الحرارية لدراسة تأثير المعاملة الحرارية على خواصها الميكانيكية والتي تتضمن: معامل مرونة، مقاومة الشد، مقاومة الصدمة، وجهد الكلال. وقد بينت النتائج زيادة في معامل المرونة للسبيكة المحضرة مقارنةً مع السبيكة القياسية بمقدار 2% تقريباً. بينما أعطت السبيكة المعاملة حرارياً لمدة 6 ساعات ومبردة بالماء مقداراً أعلى لمقاومة الشد الأقصى مقارنة مع السبيكة قبل المعاملة. إن السبيكة التي أجريت عليها معاملة المجانسة أعطت سلوك كلال أفضل مقارنة مع السبيكة قبل المعاملة والسبائك الأخرى المعاملة حرارياً. أيضاً إن فحص الصدمة بيّن إن السبيكة المعاملة حرارياً بطريقة المجانسة قد أعطت أعلى قيمة.} }