TY - JOUR ID - TI - CUMULATIVE FATIGUE DAMAGE OF 7075 ALUMINUM ALLOY REINFORCED WITH ALUMINA AL2O3 تلف الكلال التراكمي لسبيكة الالمونيوم 7075المقوى بالالومينا AL2O3 AU - Qusay Khalid Mohammed .قصي خالد محمد PY - 2018 VL - 18 IS - 1 SP - 167 EP - 181 JO - Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد SN - 20761819 AB - The reinforcement of Aluminum alloys opens a wide range of industrial application for these alloys in areas where reduction of weight has first priority, in General this operation known as metal matrix composite (MMC). In this study the nanocomposite material were fabricated using stirring time for 6 minutes at 450 rpm stirring speed .Al-7075 alloy was the base metal and the reinforcement nanocomposite material was the Alumina Al2O3 of 10 nanometer in grain size , which is used as weight percentage (wt%) for 0.3,0.5,0.7 wt% Al2O3. The results show that the best enhancement in fatigue life and strength were occurred at 0.3 wt% of Al2O3.

فتحت عملية تقوية سبائك الالمنيوم المجال واسعا للكثير من التطبيقات في المجالات الصناعية والتي من اولوياتها ان يكون وزن المعدن او السبيكة خفيفا ، بصورة عامة فان هذه العملية تعرف (MMC) Composite Metal Matrix. تم في هذا البحث تصنيع المادة النانوية باستخدام طريقة المزج بالتحريك بسرعة 450 دورة / دقيقة وبزمن مقداره 6 دقائق . سبيكة الالمنيوم Al-7075 كانت هي المعدن الاساس اما المادة المساعدة فكانت الالومينا AL2O3بحجم حبيبي مقداره 10 نانوميتر ، اما نسب الخلط فكانت 0.7,0.5,0.3 % من الوزن. اثبت النتائج ان افضل نسبة من حيث عمر ومقاومة الكلال كانت عند نسبة 0.3% . ER -