@Article{, title={Manufacturing of porous refractories from Iraqi Kaolin by adding expanded polystyrene waste تصنيع حراريات مسامية من الكاولين العراقي باضافة مخلفات البولي ستايرين التمددي}, author={Shihab A. Zaidan شهاب أحمد زيدان}, journal={Iraqi Journal of Physics المجلة العراقية للفيزياء}, volume={16}, number={37}, pages={118-126}, year={2018}, abstract={Fabrication of porous clay refractory insulating specimens from Iraqi kaolin with different percentage of Expanded Polystyrene (EPS) waste crumbs additions were investigated. After mixing and forming by hand molding, the specimens was dried and fired at 1300 oC. The structural, physical, mechanical and thermal properties of the refractory insulating products were measured. Maximum addition of EPS (1.25 wt%) lead to reduce the linear shrinkage to less than 1.7% and increased apparent porosity up to 50 %. As well as, the density, Modulus of rupture and thermal conductivity were reduced to 1.39 g/cm3, 4.1 MPa and 0.21 W/m.K, respectively. The final outcome, addition of EPS showed good results in the formation of pores without distorting the dimensions of specimens and without any cracks. In addition, it is possible to use these thermal insulators at temperatures up to 1300 oC.

صنعت عينات مسامية عازلة حرارياً من الكاؤولين العراقي مضافاً اليه مخلفات البولي ستايرين التمددي EPS (الفلين الصناعي) بعد تفتيته الى قطع صغيرة الحجم. شكلت العينات بطريقة القولبة اليدوية بعد مزج الخليط جيداً، ثم جففت العينات وحرقت بدرجة حرارة 1300 oC. تم قياس الخصائص العزلية الحرارية للمنتج مثل الخصائص التركيبية والفيزياوية والميكانيكية والحرارية. وجد ان اقصى اضافة من EPS ((1.25 wt% ادت الى تناقص الانكماش الطولي الى اقل من 1.7 % وتزايد المسامية الظاهرية الى 50 % وان الكثافة ومقاومة الانحناء والتوصيلية الحرارية تناقصت الى 1.39 g/cm3 و 4.1 MPa و 0.21 W/m.K على التوالي. اعطت النتائج بوضوح امكانية اضافة EPS لتكوين المسامات وبدون اي تشوه في بنية العينات وعدم ظهور اي شقوق. كذلك ممكن استعمال تلك العوازل الحرارية في درجة حرارة تصل الى 1300 oC.} }