TY - JOUR ID - TI - Effect of Au doping on the Magnetic Properties of Fe3O4 NPs Prepared via Photolysis and co-Precipitation Methods تأثير تطعيم الذهب على الخواص المغناطيسية للمغناتايت النانوي المحضر بطريقة التشعيع الضوئي والترسيب الكيميائي AU - Zaid Hamid Mahmoud زيد حميد محمود PY - 2018 VL - 14 IS - 03 SP - 136 EP - 146 JO - Academic Science Journal مجلة العلوم الاكاديمية SN - 83732222 25189255 AB - In this research, Fe3O4 without Au was fabricated via photolysis method, then Au was doped together with concentration of 3 wt.% using co–precipitation method. The samples of Fe3O4 without/with Au doping were characterized utilize XRD, EDX, and TEM while the magnetic properties of the samples were determined utilizing VSM. The results showed that the resistance and the magnetic values of the samples decrease with Au doping indicating semiconducting behavior. The saturation magnetization (MS) of the sample without doping (90.23 emu/g) is much greater than that (63.55 emu/g) of the sample with doping.

في هذا البحث تم تحضير الماجنتايت بطريقة التشعيع الضوئي ومن ثم طعم بمادة الذهب بكمية %3 باستخدام طريقة الترسيب. الماجنتايت المطعم وغير مطعم بمادة الذهب تم تشخيصه باستخدام حيود الاشعة السينية، مطيافية تشتت الطاقة بالأشعة السينية و المجهر الالكتروني النافذ بينما شخص منحني التباطؤ المغناطيسي باستخدام نظام قياس الخواص المغناطيسية. بينت النتائج بوجود الخاصية المغناطيسية بدرجة حرارة الغرفة وتحضير الماجنتايت المطعم بعنصر الذهب، فضلا عن ان المقاومة والتوصيلية المغناطيسية للماجنتايت تقل عند تطعيمه بالذهب وهذا يدل على سلوك شبه موصل. واظهرت ايضا ان التشبع المغناطيسي بدون تطعيم (90.23 emu/g) اكبر من النموذج الذي تم تطعيمه . (63.55 emu/g) ER -