TY - JOUR ID - TI - FTIR and Optical Properties of NiO Doped Cr2O3 Nanopar-ticles Synthesis by Hydrothermal Method AU - Tunis B. Hassan AU - Ghuson H. Mohammed PY - 2018 VL - 29 IS - 1 SP - 168 EP - 173 JO - Al-Mustansiriyah Journal of Science مجلة علوم المستنصرية SN - 1814635X 25213520 AB - Pure and Nickel oxide doped chromium (III) oxide (Cr2O3) nanoparticals are synthesized by hydrothermal technique. The effect of dopant Ni concentration on the structural behavior of Cr2O3 nanoparticles was examined by X-ray diffraction. The average crystallite size of the synthesized nanoparticles was measured from XRD patterns using Scherrer equation and was decreased from 22nm to 12.9 nm with the increasing Nio concentration in Cr2O3 from (0, 0.01, 0.06, and 0.10). Morphologies and compositional elements of the synthesized nanoparticles were observed by the field emission scanning electron microscopy (FESEM) and energy dispersive X-ray (EDX) spectroscopy, respectively. The optical property of the samples was measured by ultraviolet - visible (UV-Vis.) absorption spectroscopy. The observed optical band gap value ranges from 2.3eV to 2.5eV for Ni doped nanoparticles.

تم تحضر اوكسيد الكروم النانوي النقي والمطعم بنيكل اوكسيد بالطريقة الهيدروحرارية المائية. تم دراسة تأثير التطعيم لتركيز اوكسيد النيكل على سلوك التركيب لجسيمات اوكسيد الكروم النانوي بواسطة حيود الأشعة السينية. تم قياس معدل الحجم البلوري للجسيمات النانوية المحضرة بواسطة حيود الاشعة السيتية باستخدام معادلة شرر وكان ينخفض من 22nm إلى 12.9 نانومتر مع زيادة تركيز اوكسيد النيكل في اوكسيد الكروم من (0، 0.01، 0.06، 0.10). وقد لوحظت مورفولوجيه والعناصر التركيبية للجسيمات النانوية المحضرة من قبل المجهر الإلكتروني المسح الضوئي الانبعاثات وطاقة التشتت الأشعة السينية التحليل الطيفي، على التوالي. تم قياس الخصائصالبصرية للعينات بواسطة الأشعة فوق البنفسجية المرئية وتتراوح قيمة فجوة البصرية من 2.3 الكترون فولت إلى 2.5الكترون فولت لجسيمات اوكسيد النيكل المطعمة. ER -