@Article{, title={Effect of SiC particulates on fracture toughness of an Al-1.5% Mg matrix composite.}, author={Ali Ismail Salih}, journal={journal of the college of basic education مجلة كلية التربية الاساسية}, volume={18}, number={73 / ملحق}, pages={63-72}, year={2012}, abstract={The fracture toughness of the SiC-Al-1.5%Mg PMMCs has been studies. The MMCs were prepared by conventional method's the stir cast. The SiC preheated particle content was varied from 2, 4, 6 to 8 wt% and their average size was 53µm. we have noticed that the fracture toughness was decreased due to the increase in SiC wt%. Also the hardness has been investigated and show the hardness of the composite material was increased with the increases in the SiC wt%.The X-ray diffraction test was also investigated to the matrix alloy, SiC particle and the reinforcement material in order to study the phases which are produced into the MMCs structure. Its show that there is good contact has been produced between them.

ان متانة الكسر للمادة المركبة SiC-Al-1.5%Mg PMMCs قد درست في هذا البحث. والذي حضرت فية المواد المركبة عن طريق الخلط الميكانيكي بواسط الخلاط للحبيبات السيراميكية في المنصهر المعدني. وكانت نسب الاضافة للحبيبات السيراميكية هي 2، 4، 6، و 8 wt% مع معدل للحجم الحبيبي 53µm ، وقد لوحظ ان متانة الكسر للمادة المركبة قد انخفضت نتيجة لزيادة النسبة المئوية لحبيبات SiC مقارنة مع المادة الاساس . وكذلك لوحظ ان الصلادة قد ارتفعت نتيجة زياد النسبة المئوية لحبيبات SiC. قد تم اجراء فحص حيود الاشعة السينية للمادة الاساس واللحبيبات السيراميكية والمادة المركبة لمعرفة الاطوار الناتجة خلال عملية انتاج المادة المركبة . وقد لوحظ انة قد حصل تفاعل بيني مناسب لتوليد ربط بين المادة الحبيبية والمادة الاساس.} }