TY - JOUR ID - TI - Improving Wear Properties of 392 Al Alloy Using Centrifugal Casting تحسين خواص البلى لسبيكة المنيوم 392 باستخدام السباكة بالطرد المركزي AU - Akeel Dhahir Subhi عقيل ظاهر صبحي AU - Adnan Mohsen Abd عدنان محيسن عبد PY - 2019 VL - 15 IS - 1 SP - 63 EP - 70 JO - Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية SN - 18181171 23120789 AB - The microstructure and wear properties of 392 Al alloy with different Mg contents were studied using centrifugal casting. All melted alloys were heated to 800 ºC and poured into the preheated centrifugal casting mold (200-250 ºC) at different mould rotational speeds (1500, 1900 and 2300 r.p.m). It is clear from the results obtained that wear rate was dependent on the Mg content, applied load and mould rotational speed. Furthermore, wear test showed that the minimum wear rate was found in the inner layer of produced rings at mould rotational speed of 1900 r.p.m and Mg content of 5%.

تم في هذا البحث دراسة التركيب المجهري وخواص البلى لسبيكة المنيوم 392 والتي تحتوي على نسب مغنسيوم مختلفه باستخدام سباكة الطرد المركزي. اذ تم صهر جميع السبائك في درجة حراره 800 م° وصبت في قالب الطرد المركزي اللذي سخن مسبقا ضمن مدى حراري يتراوح بين 200-250 م° بسرع دورانية مختلفة (1500 ,1900 و2300) دوره/دقيقه .اوضحت النتائج ان معدل البلى والصلاده يعتمدان على محتوى المغنسيوم والحمل المسلط علاوة على السرعه الدورانيه للقالب. اضافة لذالك فان اختبار البلى اظهر ان اقل معدل للبلى لللطبقه الداخليه للحلقات المنتجه كان عند سرعة دورانية للقالب 1900 دوره/دقيقه, وعند نسبة مغنسيوم 5%. ER -