TY - JOUR ID - TI - Kinetics and Mechanism of Hydrogen Sorption in Yttrium-Silicon D88- Structure Phases, Part I AU - Jabbar S.Hadi AU - Tahseen A. Alsalim AU - M. Y. Shareef AU - I. J. McColm AU - Mouaid A. Hassen PY - 2009 VL - IS - 36 SP - 667 EP - 679 JO - Iraqi National Journal Of Chemistry المجلة العراقية الوطنية لعلوم الكيمياء SN - 22236686 AB - AbstractA relationship between the size of the z-axis lattice parameter and the rate of hydrogenation of D88 phases has been established. Materials with c-axis in the range 0.632-0.642 nm are most resistant to hydrogen content increase whilst maintaining a fast sorption capability for 0.9-10 H (fu)-1. From this Y5Si2Ge and Y5Si2GeN0.1 have been prepared and used to establish the hydrogen sorption kinetics at a range of temperatures and pressures of hydrogen. The effect that nitrogen has on the alloy is to increase reaction rates by a factor of approximately 3. Thermogravimetric plots were first analysed by the J-M-A equation as used by Goudy (6). Arrhenius representation of the first and second order equations indicate a significant change in reaction mechanism at 740-745 K. Activation energies are in the range 84-166 kJ (mol)-1 depending on order and temperature.

الخلاصة تم في هذا البحث ايجاد علاقة بين معامل شبكية المحور –Z وسرعة هدرجة اطوار D88 . ان المواد التي تمتلك المحور -C ضمن المدى 0.632-0.642 نانوميتر هي الكثر مقاومة لزيادة محتوى الهيدروجين . وانطلاقا من ذلك تم تحضير كل من Y5Si2Ge و Y5Si2GeN0.1 واستخدمت لتحديد مركبات امدصاص الهيدروجين ضمن مدى من درجات الحرارة وضغوط الهيدروجين . لقد كان تاثير وجود النتروجين في السبيكة هو زيادة معدلات التفاعل بمعدل ثلاث مرات تقريبا . وقد تم تحليل البيانات الثرموكرافية بواسطة معادلة J – M – A المستخدمة من قبل Goudy . ER -