TY - JOUR ID - TI - The Effect of Temperature Annealing on the Electrical and Electro - Optical Properties of Cadmium Oxide Thin Films Prepared by SILAR Method تأثير التلدين الحراري على الخواص الكهربائية والكهروضوئية لأغشية اوكسيد الكادميوم المحضرة بطريقةSILAR AU - Hayder Mohammad Ajeel حيدر محمد عجيل AU - Ashwaq Abdul- Hussain Jabor اشواق عبد الحسين جبر AU - Mohammad Khammas Khalaf محمد خماس خلف AU - Abdul- Hussain Khudair litaif عبد الحسين خضير لطيف PY - 2014 VL - 5 IS - 1 SP - 76 EP - 80 JO - Iraqi Journal of Science and Technology المجلة العراقية للعلوم والتكنولوجيا SN - 18136893 29584604 AB - Cadmium oxide thin films have been prepared on glass substrate at 363K temperature by SILAR (successive ionic layer adsorption and reaction)technique using cadmium acetate solution . The CdO thin films were annealed at 673 and 773 K under atmosphere for 45 min. The electrical and electro – optical properties were studied. Electrical studies showed that the thermal-electrical conductivity and activation energies influenced by thin films annealing . The photoconductivity of CdO thin film for annealed and non- annealed films are studied. It was found that electrical conductivity increased with annealing temperatur

حضرت اغشية اوكسيد الكادميوم على قواعد زجاجية بدرجة حرارة 363K بتقنية SILAR و باستخدام محلول خلات الكادميوم . لدنت الاغشية المحضرة بدرجتي حرارة673 ,773K و 45 min. في الهواء . دُرســت الخصائص الكهربائية والكهرو بصرية للأغشية المحضرة , الدراسات الكهربائية اشارت الى توصيل الكتروني حراري وان طاقة التنشيط الحرارية تتأثر بالتلدين الحراري للأغشية المحضرة . ودرست خصائص التوصيل الضوئي لأغشية (CdO ) الملدنة وغير الملدنة حراريا ومن خلال قياسات ( تيار – جهد ) في حالة الظلام والاضاءة و تبين ان المعاملة الحرارية تؤدي الى زيادة التوصيل الكهربائية لهذه الاغشية ER -