TY - JOUR ID - TI - Manufacturing of Erosion Measuring Rig for Polymers and Their Composites with some Experimental Results تصنیع جهاز قیاس التعریة للمواد البولیمریة ومتراکَّباتها مع بعض النتائج التجریبیة AU - Abdullhaqq A. Hamid عبدالحق عبدالقادر حامد AU - Ahmed W. Khalid احمد وليد خالد PY - 2019 VL - 24 IS - 2 SP - 115 EP - 129 JO - AL-Rafidain Engineering Journal (AREJ) مجلة هندسة الرافدين SN - 18130526 22201270 AB - Solid Particle Erosion System was manufactured as a laboratory and according to the ASTM G76 specifications in a horizontal position with a feeder screw, as the system consists of the main parts: air compressor, voltage regulator, and rubber connection hoses. And the main parts of the rig: nozzle, screw, DC motor, transmission pipes, and Installation platform. The nozzle was made of low alloy steel and hardened by water-quenching, and the conical nozzle cavity was made to insert sand into the nozzle barrel. Tolerance was chosen between the screw and cylinder in practice, with a tolerance of (4 mm) out of two experiments that were tried (2, 4 mm). So, the tolerance was chosen based on the used particles (erodent) in different ranges (150-350 µm), (350-500) µm) and (500-710 µm), preferably a tolerance that gives a smooth spin rotation. One of the things to consider is the stability of the sand flow rate and the issue of overflow or vice versa is the occurrence of a stop flow, and taking into consideration the calibration between the spin rotation and the pressure of the air. Also, the sizes of sand particles used can determine several things, including tolerance, the diameter of the nozzle barrel, and the velocity of particles that can be taken. The rig was tested for specimens of unsaturated polyester (UP) and its composites reinforced with (5 wt. %) of silicon carbide, where the experiment was carried out at an impingement velocity (25.2 m / s) and impingement angles (30°, 60°, 90°) and the size of the erodent from sand Silica has a size of (350-500 µm), so the results showed that the polyester gave the highest erosion rate at the angle (90°), which indicates its brittle behavior, while its composites gave the highest erosion rate at the angle (60°), which indicates its semi-ductile behavior. It is comparing the results obtained with previous research that shows that the rig gave positive results, and it can measure the rate of erosion of polymeric materials and their composites.  

تم تصنیع منظومة فحص سلوک التعریة بالحُبیبات الحاکة (Solid Particle Erosion) مختبریاً وحسب مواصفات (ASTM G76) ذی الوضعیة الأفقیة بمغذی من النوع اللولبی (feederscrew),إذ تتکون المنظومة من الأجزاء الرئیسیة: ضاغطة هواء, منظم فولتیة, وخراطیم توصیل مطاطیة. واجزاء اساسیة للجهاز: القاذف, واللولب, ومحرک تیار مستمر, وانابیب نقل, ومنصة تثبیت. فقدتم صناعة القاذف (nozzle) من سبیکة الفولاذ المنخض (low alloy steel) وتمت تقسیته بطریقة (water-quenching), وتم عمل تجویف القاذفالداخلی مخروطی الشکل لیعمل على ادخال الرمل الى ماسورة القاذف. وتم اختیار السماحة (tolerance)بین اللولب والاسطوانة عملیاً بسماحة (4 mm) من اصل سماحتین تمت تجربتهما (2,4 mm), فتم اختیار السماحة على اساس الحُبیبات المستعملة (erodent) بمدیات مختلفة (150-350 µm)و(350-500 µm) و(500-710 µm), فافضل سماحة التی تعطی سلاسة بدوران اللولب. ومن اهم الامور التی یجب مراعاتها هی ثبات معدل تدفق الرمل, ومسألة التدفق العالی (over flow) او العکس هو حدوث توقف للتدفق, ومراعاة المعایرة بین دوران اللولب وضغط الهواء المسلط. واخذ بنظر الاعتبار احجام حُبیبات الرمل المستخدم لتحدید عدةامور منها السماحة وقطر ماسورة القاذف والسرع التی یمکن اخذها. وتمت تجربة الجهاز لنماذج من البولستر الغیر المشبع ومتراکَّباته معزَّزة بنسبة (5 wt.%) من کربید السیلیکون, حیث تمت التجربة عند سرعة صدم (25.2 m/s) وزوایا صدم (30°,60°,90°)وحجم حُبیبات حاکة من رمل السیلیکا بحجم (350-500 µm), فکانت النتائج ان البولستر اعطى اعلى معدل تعریة عند الزاویة (90°) مما یدل على سلوکه الهش, بینما اعطى متراکَّبه اعلى معدل تعریة عند الزاویة (60°) مما یدل على سلوکه الشبه مطیلی. ومن مقارنة النتائج المستحصل علیها مع بحوث سابقة تبین ان الجهاز اعطى نتائج ایجابیة, ویمکن ان یقیس معدل التعریة للمواد البولیمیریة ومتراکَّباتها. ER -