TY - JOUR ID - TI - Reinforcement Effect of Alumina and Silica on the Mechanical Properties of Mixture Polyesters (Unsaturated Polyester / Polyurethane) تأثير التدعيم بمساحيق الألومينا والسليكا على الخصائص الميكانيكية للخليط البوليمري (بولي أستر غير مشبع/بولي يوريثان) AU - Haneen M. Ali حنين محسن علي AU - Raad A. Rasool رعد أحمد رسول AU - Soham Y. Moustafa سهام يونس مصطفى PY - 2020 VL - 29 IS - 2 A SP - 51 EP - 63 JO - Rafidain journal of science مجلة علوم الرافدين SN - 16089391 AB - In this study composite materials were prepared from based polymer mixture (B) (UPE/PU, 95/5) supported by alumina powders and silica with grain sizes (75 - 150) μm, these samples were tested B and B1, B2 and B3 respectively. The samples were subjected to mechanical tests represented by bending test, compression, hardness and impact at laboratory temperature. The results showed that the Young modulus of bending test increased by increasing the strength, and the fracture resistance was reduced by increasing the reinforcement. As for compressive resistance, the maximum compressive resistance was for alumina - supported (B1) sample 51.29 MPa. The Hardness was increased by increasing reinforcement with a maximum value of 94.5 Hs.

تم في هذه الدراسة تحضير مواد متراكبة ذات أساس من الخليط البوليمري (B) (UPE/PU, 95/5) المدعم بمساحيق الألومينا والسليكا ذات الحجم الحبيبي µm (75 - 150). بعدها تم اختبار النماذج المحضرة وهي الخليط البوليمري (B) والمواد المتراكبة المحضرة من تدعيمه (B1,B2,B3)، إذ خضعت هذه العينات لاختبارات ميكانيكية المتمثلة باختبار الانحناء (Bending Test) والإنضغاط (Compression) والصلادة (Hardness) والصدمة (Impact) عند درجة حرارة المختبر. أظهرت نتائج الاختبارات بأن أكبر قيمة لمعامل يونك من اختبار الانحناء كانت 6.15 GPa في العينة B2، وإن مقاومة الكسر قلت مع زيادة التدعيم. أما بالنسبة لمقاومة الإنضغاط فإن أقصى مقاومة انضغاط كانت للعينة B1 المدعمة بالألومينا، حيث بلغت قيمتها 51.29 MPa. أما الصلادة فقد ازدادت مع زيادة التدعيم حيث بلغت أقصى قيم لهما 94.5 Hs. ER -