@Article{, title={IRRADIATION EFFECT IN CdSe THIN FILMS /تاثيرالتشعيع على اغشية CdSe الرقيقة}, author={Eman M. Noori ايمان محمد نوري}, journal={Journal of College of Education مجلة كلية التربية}, volume={1}, number={1}, pages={69-76}, year={2019}, abstract={AbstractCadmium selenide thin films of thickness 200 nm were thermally deposited by vacuum evaporation method at room temperature on glass ground. The effects of irradiated time on the structure and optical characteristic of these films were studied. The films are hexagonal structure confirmed by XRD analysis. XRD pattern of the irradiated film at 72 hour shows an improvement of crystallinity. The optical measurements of CdSe films were carried out in the wavelengths range from 300-900 nm. The transmitance spectra shows that irradiated samples are less transmittance than non – irradiated one. The increase in irradiated time leads to a decreases in energy band gaps from 2.49 eV to 2.33 eV. Keywords: Structure characteristic, Optical characteristic, irradiation, thin films, CdSe

الخلاصةرسبت الاغشية الرقيقة لسيلينايد الكادميوم ذات السمك 200 nm حراريا باستخدام طريقة التبخير بالفراغ عند درجة حرارة الغرفة على ارضيات من الزجاج. درس تاثير زمن التشعيع على الخواص التركيبية والبصرية لهذة الاغشية. تم التاكد من تركيب الاغشية السداسي بتحليل XRD. بين مخطط XRD للغشاء الملدن عند 72 ساعة تطورات في التبلور. الصفات البصرية لاغشية CdSe سجلت بواسطة مطياف – UV. بين طيف النفاذية ان النماذج المشععه اقل نفاذية من الغير مشععة. زيادة زمن التشغيغ قاد الى تناقص فجوة الطاقة من 4.49 eV الى 2.33 eV.الكلمات المفتاحية: الصفات التركيبية, الصفات البصرية, التشعيع, الاغشية الرقيقة, سيلينايدالكادميوم} }