TY - JOUR ID - TI - Galvanic Corrosion Behavior of Electroless Nickel Coating in Al-Zubare Harbor-Water AU - Mohammed Hliyil Hafiz PY - 2007 VL - 25 IS - 9 SP - 1056 EP - 1063 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - Electrode potentials in AL-Zubare harbor water (South -Gas Company),of 23.88 ohm-cm at 20oC were reported for 26 metals and alloys includingvalues for electroless nickels that signify a greater passivity than steel. Thelarge potential difference between steel and electroless nickel predicts severegalvanic corrosion, which was confirmed by weight loss data for coupled steeland electroless nickel electrodes immersed in AL-Zubare Harbor water(South -Gas Company, 23.88 ohm-cm at 20oC) .Changes in the phosphorouscontent in the range of 7.10 to 12.45 percent had only a slight effect on theelectrode potential of electroless nickel.This study indicates the beneficial use of electroless nickel coating is morepassive than other (metals and alloys) and that galvanic corrosion of activemetals such as steel can be severe .

سجلت قيم الجهد الكهربائي المقاس في مياه ميناء الزبير (الخاص بشركة غازالجنوب ذو المقاومة الكهربائية 23.88 أوم – سم بدرجة حرارة 20 مئوية) ل ( 26 ) معدنوسبيكة بضمنها الطلاء بالنيكل اللاكهربائي والذي دل على خمولية أكثر من الفولاذ. كان فرقالجهد الكهربائي الأكبر بين الفولاذ والنيكل اللاكهربائي ينبئ بشدة التآكل الكلفاني والذي تمأستخراج قيمه من البيانات الخاصة بفقدان الوزن لمزدوج أقطاب الفولاذ والنيكل اللاكهربائيالمغمورة في مياه ميناء الزبير. أن تغيير نسبة المحتوى الفسفوري ضمن المدى ( 7.1 إلى12.45 %) كان له تأثير قليل نسبي على مقدار الجهد الكهربائي لقطب النيكل. تشير الدراسةإلى فائدة استخدام طريقة الطلاء بالنيكل اللاكهربائي لكونه أكثر خمولية من بعض المعادنوالسبائك وان التآكل الكلفاني شديد للمعادن الفعالة مثل الفولاذ ER -