@Article{, title={Improvement of Locally Produced Low- Density Polyethylene}, author={Najat .J.saleh and Zanaib.Y.shnean}, journal={Engineering and Technology Journal مجلة الهندسة والتكنولوجيا}, volume={26}, number={9}, pages={1061-1067}, year={2008}, abstract={In the present work, a polymer composite was fabricated by mixing LDPEwith different wt% of pigment (Fe2O3 and TiO2) to obtain desirable properties infabrication single screw-extruder was utilized , this mixing machine operated at atemperature between (150-170)Co.some of mechanical properties, such as tensile,impact, hardness and bending test were determined at different weight fraction ofcomposite materials. It was found that the addition of pigment (TiO2 and Fe2O3) to theLDPE leads to increase the modulus of elasticity, tensile strength, tensile strength atbreak, shore hardness on other hand it decreases the % elongation at break, and for theimpact strength.

في البحث الحالي تم تصنيع المواد المتراكبة بواسطة مزج البولي اثلين الواطئ الكثافة معنسب وزنية مختلفة من (ثنائي اوكسيد التيتانيوم ، اوكسيد الحديد )وذلك لإيجاد أحسن الخصائص١٧٠ ) درجة - باستخدام جهاز الباثقة الأحادية حيث تم تشغيلها عند درجات حرار ة تتراوح بين ( ١٥٠مئوية.تم أجراء العديد من الفحوصات (الاتلافية)حيث تم أجراء فحص الشد،الصدم،الصلادة والانحناءعلى النماذج المحضرة ووجد إن إضافة مزيج من ثنائي اوكسيد التيتانيوم ،اوكسيد الحديد إلى البولياثلين واطئ الكثافة قد أدى إلى زيادة كل من معامل المرونة ،إجهاد الشد ،إجهاد الشد عند الكسروتقليل النسبة المئوية للاستطالة عند الكسر .أما بالنسبة إلى فحص الصدم فقدد وجد إن إضافة ثنائياوكسيد التيتانيوم واوكسيد الحديد إلى البولي اثلين الواطئ الكثافة قد أدى إلى تقليل مقاومة الموادللصدم.لذلك فان البولي اثلين الواطئ الكثافة وبد ون إضافة قد أعطى أعلى قيمة للصدم .} }