TY - JOUR ID - TI - Study of the Mechanical Properties by Using Thermo- Mechanical Processing of Alloy Steel تحسين الخواص الميكانيكية باستخدام المعاملة الحرارية الميكانيكية للفولاذ السبائكي AU - Mahdi Mutar Hanoon AU - Mohammed H. Hafiz AU - Amin D. Thamir PY - 2010 VL - 28 IS - 8 SP - 1692 EP - 1705 JO - Engineering and Technology Journal مجلة الهندسة والتكنولوجيا SN - 16816900 24120758 AB - The purpose of this work is to study the effects of thermo mechanicaltreatments to improve mechanical properties of the alloy steel (DIN 42 Cr Mo4), suchas tensile strength, toughness, and hardness. All mechanical factors affected by themetallurgical changes in alloy like microstructure refinement and appearing newphases are thoroughly discussed.Heating was done in induction furnace at 1150oC and specimens were forgedin temperature of 1000oC but the forging process was done with different forgingloads (deformation percentage) with values of (800, 1000, 2500 and 4000 tons) with adeformation percentages of (26%, 31%, 45% and 61%) respectively.

تكمن الغاية من البحث دراسة تأثير المعاملات الحرارية الميكانيكية العالية لتحسين الخواصكمقاومة الشد ، المتانة والصلادة. تت أثر جميع ، (DIN 42 Cr Mo الميكانيكية لسبيكة الفولاذ ( 4عوامل التآكل والعوامل الميكانيكية بالمتغيرات الميتالورجية كالتنعيم الحبيبي وظهور الأطوار الجديدةالتي تم مناقشتها بشكل تفصيلي.تمت عملية التسخين في فرن حراري حثي وبدرجة حرارة 1150 درجة مئوية ومن ثم تم، طرق العينات بدرجة حرارة مقدارها 1000 درجة مئوية لكن بأحمال طرق مختلفة وهي ( 800(% 45 % و 61 ،%31 ،% 4000 طن) وبمكبس طرق وكانت نسب التشكيل ( 26 ،2500 ،1000على التوالي.أجريت الفحوصات الميكانيكية لجميع لعينات قبل وبعد المعاملة الحرارية الميكانيكية، والتيتضمنت فحص أجهاد مقاومة الشد ، فحص الصلادة وفحص المتانة. أفضل خواص ميكانيكة تم(% الحصول عليها وذلك عند أستخدام حمل طرق مقداره ( 1000 طن) أي بنسبة تشكيل مقدارها ( 31ومتانة بقيمة HV حيث كانت مقاومة أجهاد الشد 755 نيوتن/ملم 2 وبصلادة مقدارها 21541.3 جول. ER -