TY - JOUR ID - TI - EFFECT OF FLAME RETARDANT MATERIAL ADDITION ON THERMAL CONDUCTIVITY OF POLYMERIC COMPOSITE MATERIAL REINFORCED BY FIBERS تأثير إضافة مادة معيقة للّهَب على الموصلية الحرارية لمادة مركبة بوليميرية مقواة بالألياف AU - سليم جاسم عباس PY - 2011 VL - 24 IS - 6 SP - A1 EP - A6 JO - Journal of Techniques مجلة التقني SN - 27088383 AB - This research studied the effect of flame retardant material addition namely antimony trioxide (Sb2O3) on thermal conductivity of composite material consist of conbextra epoxy (EP-10) resin reinforced biaxially by woven roving E–type glass fibers (°45-°0) with density (600g/cm3) .The effect of different percents of antimony trioxide (10%, 20%,30%) on thermal conductivity was investigated by using Fourier equation to calculate the thermal conductivity coefficient (k) for this composite material before and after addition of flame retardant material ,where the thermal conductivity value improved after added trioxide and the best increment in conductivity was at (30%) from antimony trioxide .

تم في هذا البحث دراسة تأثير إضافة مادة معيقة للّهب وهي أُوكسيد الأنتيمون الثلاثي( Sb2O3 ) على الموصلية الحرارية لمادة مركبة مكونة من راتنج الإيبوكسي نوع كونبكسترا (EP-10) المقوى بألياف الزجاج بشكل ظفائر محاكة ثنائية الإتجاه (45º- 0º) نوع (E-Glass) ذات كثافة سطحية (600g/cm3) . لقد تم إضافة أُوكسيد الأنتيمون الثلاثي بنسب مختلفـة (%30, %20,%10) إلى المادة المركبة النهائية وقياس مدى تأثر الموصلية الحرارية لهذه المادة عن طريق إستخدام معادلة فورير لحساب التغير في قيمة معامل التوصيل الحراري (k) للمادة المركبة قبل وبعد إضافة المادة المعيقة للّهب ، ومن خلال النتائج التي تم الحصول عليها تحسنت قيمة الموصلية الحرارية بعد إضافة الأُوكسيد الثلاثي إليها وأفضل زيادة في الموصلية كانت عند نسبة (%30) من أُوكسيد الأنتيمون الثلاثي . ER -