TY - JOUR ID - TI - Effect of annealing temperature on the formability of low carbon steel sheet" تأثير درجة حرارة التخمير على قابلية التشكيل لصفيحة من صلب منخفض الكربون AU - Ahmed S.Abdulaziz احمد سعدون عبد العزيز PY - 2010 VL - 18 IS - 4 SP - 44 EP - 50 JO - AL-Rafidain Engineering Journal (AREJ) مجلة هندسة الرافدين SN - 18130526 22201270 AB - AbstractThis research include a practical study on the effect of pre-annealing in different conditions and the number of forming steps on the formability of low carbon steel sheet of thickness(10)mm which is widely used due to popular industrial uses especially in the cold pressing processes. A particular specimens were annealed at different temperatures then a set of tests were applied on these specimen. It was noticed that the annealing improve the ductility of the specimens especially the temperature that equal to 550°C with (12) minute soaking time which gave the best ability of cold pressing for the specimen . Also it was found that use of two steps of cold pressing with annealing between improve the formability of the specimen as compared with the single step of cold pressing. Key words :annealing , steel , forming , cold pressing , ductility.

الخلاصةيتضمن هذا البحث دراسة عملية حول تأثير كل من الظروف المختلفة لعملية التخمير المسبق وكذلك عدد مراحل الكبس المستخدمة على قابلية التشكيل(الكبس) لصفيحة من صلب منخفض الكربون ذات سمك (1) ملم وذلك بسبب الاستخدامات الصناعية الشائعة لهذا النوع من الصلب في عمليات التشكيل المختلفة ومنها عملية الكبس البارد.أجريت عملية التخمير المسبق على نماذج محددة الأبعاد وأجريت مجموعة من الاختبارات عليها فلوحظ من خلال النتائج العملية حصول ازدياد في المطيلية للنماذج بسبب التخمير المسبق ، وان أفضل قابلية للكبس البارد للصفيحة تحققت عند درجة حرارة تخمير مقدارها (550)°م وبفترة زمنية للإبقاء مقدارها(12) دقيقة كما لوحظ أيضا أن إجراء الكبس البارد على مرحلتين يتخللها إجراء التخمير بالظروف أنفة الذكر يعطي قابلية كبس أفضل مقارنة باجراءه على مرحلة واحدة فقط. ER -