TY - JOUR ID - TI - STATE SOME MECHANICAL PROPERTIES FOR Al- ALLOY WELDED BY SEAM WELDING TECHNIQUE حالة بعض الخواص الميكانيكية لسبائك الألمنيوم الملحومة بطريقة اللحام الخطي AU - Latfe Y .Zedan لطفي يوسف زيدان PY - 2010 VL - 3 IS - 1 SP - 80 EP - 90 JO - DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية SN - 19998716 26166909 AB - The aim of this paper was perpetrated lap joint welding samples welded by seam welding method ,2014 heat treatable aluminum alloy ,the paper studied some groups at different variable welding ,welding time was studied at electrode pressure 1,1.5 KN with thickness 1.5 mm and another group at 2 mm .after welding process shear strength ,Vickers hardness were tested at different variables.The paper stated the best shearing strength at 1.5mm thickness with 45 KA welding current at 1.5 KN electrode pressure. Increase 0.5 mm in thickness lead to decrease 20% of shearing strength.

تهدف الدراسة الحالية إلى تحضير وصلات لحام تراكبية ملحومة بطريقة اللحام الخطي ,حيث تم استخدام سبيكة الألمنيوم (2014) القابلة للتعامل الحراري ,تم دراسة متغيرات عملية اللحام وفق مجاميع مختلفة . تم دراسة زمن اللحام عند ضغط اليكترود ،KN(1,1.5) بسمكmm 1.5 والمجموعة الأخرى بنفس الظروف ولكن بسمك (2MM) وبعد إجراء عملية اللحام تم حساب مقاومة القص بالظروف المختلفة وكذلك حساب الصلادة المجهرية عند خط اللحام وبجانبه .ومن الدراسة لوحظ أن أفضل مقاومة قص لوصلة اللحام كانت عند سمك mm 1.5 وتيار لحام KA45 عند 1.5 KN ضغط اليكترود. كما لوحظ أن زيادة السمك بmm 0.5 تنخفض قيمة مقاومة القص إلى 20%. ER -