TY - JOUR ID - TI - Some gas sensing properties of PbS thin films بعض خصائص تحسس الغازات لأغشية PbS الرقيقة AU - Resoul H.Mukalaf رسول حسين مخلف AU - Emad.J.Mahdim عماد جليل مهدي AU - Ahmed . A. hamad أحمد عاصي حمد AU - Ashwaq .A.jabor أشواق عبدالحسين جبر AU - Morooj.A. Abood مروج علي عبود PY - 2011 VL - 9 IS - 15 SP - 63 EP - 67 JO - Iraqi Journal of Physics المجلة العراقية للفيزياء SN - 20704003 26645548 AB - In this research PbS thin film have been prepared by chemical bath deposition technique (CBD).The PbS film with thickness of (1-1.5)μm was thermally treated at temperature of 100°C for 4 hours. Some Structural characteristics was studied by using X-ray diffraction (XRD)and optical microscope photograph some of chemical gas sensing measurements were carried out ,it shown that the sensitivity of (CO2) gas depend on the grain Size and deposition substrate. The grain size of PbS film deposited on on glass closed to 21.4 nm while 37.97nm for Si substrate. The result of current-voltage characterization shwon the sensitivity of prepared film deposited on Si better than film on glass.

في هذا البحث حضرت أغشية PbS بتقنية الترسيب الكيمياوي عند سمك(1-1.5) m وعوملت الأغشية حرارياً عند درجة حرارة 100C لمدة أربعة ساعات. درست بعض الخصائص التركيبية بإستخدام جهاز X-ray والمجهر الضوئي،اما بالنسبة لفحوصات المتحسسات الغازية أثبتت أن التحسسية تعتمد على الحجم الحبيبي ونوع الأرضية المرسبة عليها الأغشية. الحجم الحبيبي للأغشية PbS المرسبة على الزجاج كانت مساوية لـ nm 21.4 بينما الأغشية المرسبة على السليكون تساوي 37.97 ، النتائج أظهرت أن خصائص التيار- فولتية والتحسسية للأغشية المرسبة على الـ Si أفضل مما عليه في الزجاج. ER -