TY - JOUR ID - TI - Porosity Control During Preparation of Bronze Filter Materials by Powder Metallurgy AU - Saleh K. Jabur AU - Adnan S. Jabur PY - 2011 VL - 2 IS - 1 SP - 85 EP - 102 JO - University of Thi-Qar Journal for Engineering Sciences مجلة جامعة ذي قار للعلوم الهندسية SN - 26645564 26645572 AB - The ability to achieve close control of porosity and pore size is the main reason that filters are produced by powder metallurgy. This study was performed using bronze alloy powder (Cu-7.5%Sn- 0.1%Fe-0.3%Pb-0.15%Zn). The samples were prepared by two methods :(1) cold die compacting at different particle size, compacting pressure, sinteringtime, and sintering temperature, and (2) loose powder sintering. The compacts were sintered under controlled atmosphere. After surface preparation of the samples, the microstructure was used to compute the apparent porosity. It was found that the(Loose Powder Sintering) methodis optimum method to produce highly porous materials with (~59%) porosity when selecting the proper conditions. The porosities obtained using cold die compaction are ranging between (5-41%) and sintered density ranging between (58.6-94.3%) of the theoretical mean density ofthe starting materials.

أن السبب الرئیس في استخدام المرشحات ألمصنعة من مساحیق المعادن ھوقابلیة الحصول على نسبة مسامیة مسیطر علیھا. الدراسة أنجزت باستخدام سبیكة برونز على شكل مسحوق. تم تحضیر النماذج بطریقتین:( ١) كبس على (Cu-7.5%Sn- 0.1%Fe-0.3%Pb-0.15%Zn) البارد عند ضغوط كبس مختلفة وحجم حبیبات المسحوق مختلفة Loose Powder كذالك زمن وحرارة التلبید مختلفین, ( ٢) الطریقة الأخرى لتحضیر العینات ھي المكبوسات لبدت في جو مسیطر علیھ. بعد تحضیر السطح, العینات عولجت لحساب المسامیة الظاھریة. لقد .Sinteringعند (Loose Powder Sintering) وجد أن الطریقة الأفضل لإنتاج المواد ذات المسامیة العالیة حوالي (% 59 ) ھي (5- استخدام الظروف الملائمة. المسامیة التي تم الحصول علیھا باستخدام كبس على البارد والتلبید تتراوح بین(% 4158.6 ) من الكثافة النظریة للمادة الخام. - والكثافة تتراوح بین (% 9 ER -