@Article{, title={Effect of Tempering Temperature on Wear Rate of Steel 100Cr6 تاثير درجة حرارة المراجعة على معدل البلى لفولاذ 100Cr6}, author={khansaa D.Al-shamari خنساء الشمري and Aseel Bassim Al-zubaydi اسيل باسم الزبيدي and Khalid Abdul Al-hassan خالد عبد الحسن}, journal={Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد}, volume={11}, number={3}, pages={550-559}, year={2011}, abstract={AbstractThis research aims to study the effect of quenching by oil with tempering at180°C and 400°C on wear rate of 100Cr6 steel. A pin-on-disc technique was used tomeasure wear rate at different loads and different sliding times with constant slidingspeed(2.199msec)and the hardness of steel dise was 45HRC.The results show that the wear resistance of the specimen quenched by oil andtempered at 400°C was more than the specimen quenched by oil and tempered at180°C.

الملخصيهدف البحث إلى د ا رسة تأثير التقسية بالزيت ثم إج ا رء الم ا رجعة عند درجات.100 Cr 400° على معدل البلى لفولاذ 6 C 180° و C ح ا رريةوقد استخدمت تقنيه المسمار على القرص لقياس معدل البلى عند تسليط أحمال مختلفة وفت ا رت.45HRC 2.199 ) وصلادة القرص الفولاذي msec) انزلاق مختلفة مع تثبيت سرعه الانزلاقوقد أظهرت النتائج ان معدل البلى يزداد مع زيادة الحمل المسلط والفترة الزمنية للانزلاق.وكذلك400° ذات مقاومه بلى C اظهرت النتائج ان العينه المقساة بالزيت والم ا رجعة عند درجه ح ا ررة.180°C أعلى بالمقارنة مع العينة المقساة بالزيت والم ا رجعة عند درجة ح ا ررة} }