TY - JOUR ID - TI - SELF-GLAZED CERAMICS USING CHEMICAL SWELLING OF ZINC-METAL POWDER AU - Prof. Dr. Hadi S. Al-Lami PY - 2011 VL - 29 IS - 1C english SP - 60 EP - 73 JO - Basrah Journal of Science (Bas J Sci) مجلة البصرة للعلوم SN - 26648288 26648296 AB - Glazing process is considered as a very important step for a lot of unfinished ceramic wares to be suit various technical applications. An attempt was made, in this work, to use a self-glazing process. This includes mixing the necessary raw materials with the some other additives, which has the ability of producing glaze material during firing. Our ceramics were based on kaolin and silica. The promising additive to be responsible for making glaze was zinc metal powder which is known to undergo chemical swelling with dilute solution of sodium hydroxide. A well crystallized new phase of willemite produces the glaze nature to ceramics fired at high temperatures, causing an increasing in specific gravity of unformed fired powders and decreasing in porosity and water absorption and increasing in the linear shrinkage, apparent solid density and the strength of the fabricated ceramics. This was supported by X-ray and SEM examinations.

تعتبر عملية التزجيج خطوة مهمة في عملية إنتاج المواد السيراميكية، ليتلاءم المنتج السيراميكي مع مختلف التطبيقات التكنولوجية. لقد تم في هذا العمل محاولة إجراء عملية التزجيج الذاتي لخليط من الكاؤولين والسليكا بإضافة نسب وزنيه مختلفة من مسحوق معدن الزنك، الذي من المعروف بأنه يسبب في انتفاخ العينة السيراميكية نتيجة لتفاعله معها، و مكوناً طور ويلمايت (willemite) أثناء عملية الحرق. أن مادة ويلمايت معروف عنها تواجدها في حالة زجاج بلوري مؤدية إلى تزجيج كل الجسم السيراميكي. تم التأكد من ذلك بسبب الزيادة في الوزن النوعي للمسحوق المحروق غير المشكل، وكذلك النقصان في مسامية وامتصاصية الجسم السيراميكي المحروق و الزيادة في معامل التقلص، كثافة الصلب الظاهرية و في المتانة. دعمت النتائج بفحوصات الأشعة السينية والمجهر الإلكتروني الماسح. ER -