TY - JOUR ID - TI - Mechanical behaviour of Low Density Polyethylene / Shrimp Shells Composite. دراسة السلوك الميكانيكي لمتراكب البولي اثيلين واطئ الكثافة/ قشور الروبيان . AU - Abdullah A. Hussein, Abdulwahab A.Sultan and Qusay A. Matoq PY - 2011 VL - 37 IS - 3A SP - 5 EP - 11 JO - Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) SN - 18172695 2411524X AB - In the present work, the mechanical behaviour of (LDPE-463) reinforced with Shrimp Shells (Metapenaeusaffinis) composite, as a function filler contact (5, 10, 15, 20, 25, wt %). Filler concentration has an obvious effect on improving several mechanical parameters. The parameters studied are young’s modules, stress at break, and stress at yield which were increased with increasing filler concentration. Elongation as indirect results of stress at break was decreased with increasing filler concentration. It was found that the addition of Shrimp Shells to the LDPE leads to decreases impact strength. Results were analyzed in the frame of drawing model.

تم تحضير مزيج من بولي اثلين واطئ الكثافة (463) و قشورالروبيان نوع (ميتابنايص أ فانيص) غير المرغوب ، حيث لا يمتلك أي قيمة غذائية ممكن أن يستفاد منها وبنسب وزنية تتراوح (5, 10, 15, 20, 25, wt%) كداله للمالئ المضاف ، وتمت دراسة السلوك الميكانيكي لهذا الخليط. أظهرت النتائج العملية بان إضافة المالئ يعمل على تحسين الخواص الميكانيكية وذلك بزيادة قوة الإجهاد ومعامل يونك و الإجهاد عند الوهن والإجهاد عند القطع. كما وجد أن مقدار الاستطالة يقل مع زيادة تركيز المضاف. أما بالنسبة إلى فحص الصدم فقد وجد إنه يقل بزيادة نسبة المالئ .لذلك فان البولي اثلين الواطئ الكثافة وبد ون إضافة قد أعطى أعلى قيمة للصدم . تم تحليل البيانات العملية بالاعتماد على موديل السحب. ER -