TY - JOUR ID - TI - Synthesis, Structural and Optical Properties of Nanostructured ZnO Thin Films Prepared by Sol Gel Process AU - F. A. Kasim PY - 2010 VL - 36 IS - 2A SP - 16 EP - 21 JO - Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) SN - 18172695 2411524X AB - Nanostructured ZnO thin films have been synthesized by Sol Gel process. The ZnO precursors were prepared by using zinc acetate dehydrate and a mixed solution of monoethanolamine and ethanol, and were prepared with Zn2+ concentration 0.5mole. The films were deposited on glass substrates by spin coating at 3000 rpm for 30s at room temperature. These films were postheated at 400oC for 1h at air. ZnO thin films have a polycrystalline and wurtzite structure. The crystallite size was determined by X-ray diffraction using Scherrer method. The crystallite size of ZnO thin film was 23.4nm. The transmittance spectra of ZnO films were 85% in the visible region from 600 to 800nm. The energy band gap is found to be 3.24 eV for ZnO film.

حضرت اغشية أوكسيد الزنك النانوتركيبية بواسطة عملية Sol Gel. وتم تحضيرها باستخدام خلات الزنك المائية ومحلول ممتزج من احادي اثانول امين ومذيب الايثانول وقد كان تركيز Zn (0.5 مول). وتم ترسيب المادة المحضرة على الزجاج بواسطة جهاز الطلاء عن طريق التدوير Spin Coating بسرعة قدرها 3000 دورة لمدة 30 ثانية وفي درجة حرارة الغرفة وتم الاحماء النهائي للاغشية بدرجة حرارة 400oC ولمدة ساعة واحدة. تم دراسة الشكل التركيبي للاغشية باستخدام الـ XRD، اذ امتلكت الاغشية الرقيقة لاوكسيد الزنك تركيباً متعدد التبلور وتركيب wurtzite. وتم حساب حجم التبلور باستخدم حيود الاشعة السينية بواسطة معادلة شرر، اذ وجد ان حجم تبلور غشاء أوكسيد الزنك هو 23.4nm . اثبتت دراسة الخصائص البصرية لاغشية اوكسيد الزنك من ملاحظة طيف النفاذية زيادة النفاذية من 85% فما فوق عند الطول الموجي 600nm لاغشية اوكسيد الزنك بتركيز 0.5 مول. كذلك أثبتت دراسة الخصائص البصرية لأغشية اوكسيد الزنك ان فجوة الطاقة كانت (3.24eV). ER -