TY - JOUR ID - TI - Study of Annealing, Hardening and Tempering on Hardness دراسة تأثير التلدين ، التصليد والمراجعة على الصلادة والبنية المجهرية AU - Nuha. H. AL- Hasan نهى هادي الحسن PY - 2010 VL - 36 IS - 3A SP - 22 EP - 28 JO - Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) SN - 18172695 2411524X AB - In this study, the effects of heat treatments annealing ,hardening and tempering on the microstructure and hardness of Mn-Fe Alloy were investigated. The Mn-Fe alloy samples were annealed at 900◦C for 20 min then cooling inside furnace and hardened treatment at 900◦C for 20 min with cooling by water, oil, and salts solution. The specimens were subsequently tempered at temperatures of 100 oC, 290 oC, 350 oC and 500oC. The microstructures, and hardness properties of these samples were analyzed and compared with samples without treatment. The microscopic examinations showed that difference in grains size for samples before and after heat treatments. The result showed that tempering of Mn-Fe Alloy samples (0.3%C) significantly exhibited better hardness as compared with that of Mn-Fe alloy without treatments .

في هذه الدراسة ، تم التعرف على تأثير المعاملات الحرارية :التلدين، التصليد والمراجعة على البنية المجهرية وخاصية الصلادة في سبيكةMn – Fe . عينات سبيكة Mn – Fe لدنت بدرجة حرارة 900◦C لمدة 20 min وبردت داخل الفرن وعوملت بالتصليد بدرجة حرارة 900◦C لمدة 20 min وبردت في الماء والزيت ومحلول ملحي. بعدها تم مراجعة العينات في درجات الحرارة من 100 oC 290oC, 350 oC, و 500oC .تم تحليل البنى المجهرية وخاصية الصلادة لهذه السبيكة ومقارنتها مع عينة من دون معاملة ، تم فحص البنى المجهرية للعينات قبل المعاملة الحرارية وبعد تغيرها . واظهرت النتائج ان معاملة سبيكةMn – Fe (0.3%C) يؤدي الى الحصول على أفضل الخصائص الميكانيكية بما في ذلك ارتفاع الصلادة بالمقارنة مع سبيكة Mn – Fe بدون معاملة. ER -