TY - JOUR ID - TI - Conduction mechanism of poly (P-Aminobenzaldehyde) terminated by phenylene diamine doped with AU - H. K. Ibrahim PY - 2007 VL - 33 IS - 2A SP - 66 EP - 75 JO - Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) SN - 18172695 2411524X AB - The electrical properties of poly (P-Aminobenzaldehyde) terminated by pheneylene diamine doped with Na2[Fe(CN)5.NO].2H2O films prepared by cast method have been investigated.The (Current – Voltage) and (Conductivity – temperature) relationships are measured in the voltage and temperature ranges (5-120) V and (288 -348) K respectively. The resistance of the doped films is found to have a negative thermal coefficient. The activation energy at temperature (288 -348)K about (0.175)eV is found from the ohmic region of the dark (current – voltage) characteristic. The conductivity at room temperature was equal to 2.5×10-14 (S.cm-1).The deviation from ohm's law has been analysed in term of the available conduction theories. Hopping conduction mechanism was concluded to be the most probable as interpreting the behavior of charge transport that supplied by injector electrodes.

تم في هذا البحث دراسة الخواص الكهربائية للبوليمر بولي (بارا – أمينو بنزلديهايد) ذي النهاية الطرفية ثنائي أمين فنيلين المشوب بمادة خماسي سيانات نتروسيل الحديدوز ثنائي الصوديوم ثنائي جزيئة الماء Na[Fe(CN)5].2H2O والمحضر بطريقة الصب.تم قياس ميزة التيار –الفولتية) وكذلك (التوصيلية – درجة الحرارة) في مدى من الفولتيات ودرجات الحرارة (5 – 120)V و (288 – 348)K على التوالي.أظهرت النتائج العملية أن مقاومة الاغشية المشوبة تمتلك معامل حراري سالب وأن طاقة التنشيط المحسوبة من خلال تحليل ميزة (التيار – الفولتية) عند المنطقة الاومية كانت قيمتها(0.175)eV. تم حساب التوصيلية الكهربائية الحجمية في درجة حرارة الغرفة وكانت قيمتها 2.5×10-14(S.cm-1). تم تحليل الانحراف عن السلوك الاومي من خلال نظريات التوصيل الكهربائي في البوليمرات الصلبة وقد وجد بأن آلية التوصيل من نوع القفز (الهوي) هي الاكثر في وصف النتائج العملية. ER -