@Article{, title={STUDY OF THE EFFECT OF NH4F CONCENTRATION ON THE STRUCTURE OF ELECTROCHEMICALLY PREPARED TiO2 NANOTUBES دراسة تاثير تركيز NH4F على تركيب الانابيب النانوية لـ (TiO2) المحضرة الكتروكيميائياً}, author={Hareith I. Jaafar حارث ابراهيم جعفر and Abdulalkareem M. A. Alsammerraei عبد الكريم محمد علي and Haidar H. Hamdan حيدر حميد حمدان}, journal={Iraqi Journal of Science المجلة العراقية للعلوم}, volume={53}, number={4}, pages={827-831}, year={2012}, abstract={In this study Titania nanotube arrays were prepared at room temperature (~25 ºC) via electrochemical anodization process of pure titanium foil in glycerol base electrolyte, different concentrations of ammonium fluoride salt (0.5 and 1.5wt.%) were added to the electrolyte as a tube enhancing agent. When anodizing Ti in 0.5 wt. % NH4F, nanotubes are formed with 54 ± 10 nm tube diameter, 20 ± 3 nm wall thickness and 1.76 µm tube length. When anodizing Ti in 1.5 wt. % NH4F, nanotubes are formed with 69 ± 10 nm tube diameter, 29 ± 3 nm wall thickness and 2.71 µm tube length. The morphology and structure of the Titania films were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), and atomic force microscopy (AFM). PACS numbers: 81.65.Mg, 82.45. +z, 81.10.-h.

في هذه الدراسة صفوف التيتانيا نانوتيوب حضرت في درجة حرارة الغرفة ~25 ºC بطريقة الانودة الكهروكيمائية لصفائح التيتانيوم النقي في محلول كهربائي اساسه جليسيرول (glycerol)، تراكيز مختلفة من ملح فلوريد الامونيوم 0.5 and 1.5wt.% اضيفت الى المحلول كعامل محسن للانبوب. عندما يؤكسد التيتانيوم في 0.5 wt%.NH4F ، كان قطر الانابيب النانوية المشكلة 10nm± 54 ، سمك الجدار nm 3± 20 و µm 1.76 طول الانبوب. عندما يؤكسد التيتانيوم في 1.5 wt%.NH4F ، كان قطر الانابيب النانوية المشكلة 10nm± 69 ، سمك الجدار nm 3± 29 و µm 2.71 طول الانبوب. تمت دراسة مورفلوجية وتركيب افلام التيتانيا بواسطة المجهر الالكتروني الماسح، مجهر القوة الذرية و حيود الاشعة السينية.} }