TY - JOUR ID - TI - Injection Temperature Effects on the Properties of High Density Polyethylene Crates تأثير درجة حرارة الحقن على خواص صناديق التعبئة المصنعة من مادة متعدد الاثلين العال الكثافة AU - Sawsan D. A. Shubbar سوسن ضياء احمد شبر PY - 2013 VL - 19 IS - 6 SP - 752 EP - 763 JO - Journal of Engineering مجلة الهندسة SN - 17264073 25203339 AB - This study was undertaken to provide more insight on the optimum injection temperature used for the production of PE crates, thereby saving time and money, and improving part quality. The work included processing trails of HDPE crates in an injection molding machine at five temperatures ranged from 220 to 300°C. Both Rheological and mechanical characterization was conducted in order to understand the effect of injection temperature on the properties of crates. Oven aging was also applied for (4 weeks) to evaluate the long-term thermal stability. The results revealed that producing the crates at a temperature range of (260-280 °C) gives the best rheological and mechanical result. The lowest drop in thermal stability has been observed for the crates produced at this temperature range.

تم اجراء هذا البحث لغرض توفير معرفة لدرجة حرارة الحقن الامثل المستعملة لانتاج صناديق البولي اثلين، وبالتالي توفير الوقت والمال وتحسين نوعية المنتج.تضمن العمل انتاج الصناديق باستعمال البولي اثلين عالي الكثافة بماكنة قولبة وحقن باستعمال خمس درجات حرارة تتراوح من 220 الى 300 درجة سلليزية .وتم قياس الخواص الميكانيكية وخواص السيولة لغرض فهم ودراسة تاثير درجات حرارة الحقن المختلفة على مواصفات الصناديق المختلفة. بالاضافة الى تعريض الصناديق الى عملية تقادم حراري في فرن ولمدة 4 اسابيع لتحديد الثبوتية الحرارية لها على المدى الطويل. افرزت النتائج ان انتاج الصناديق بالمدى 260- 280 درجة سلليزية تعطي احسن الخواص الميكانيكية وخواص السيولة ، وكذلك فان الصناديق المنتجة في هذا المدى ابدت اقل نسبة تدهور في الثبات الحراري عند فحص التقادم. ER -