TY - JOUR ID - TI - Mechanical and Tribological Behavior of Unsaturated Polyester Nan carbon Black Composite السلوك الميكانيكي والترايبولجي لمتراكب البولي استر الغير مشبع المدعم بحبيبات الكاربون الأسود النانوية AU - Amer Hameed Majeed عامر حميد مجيد AU - Mohammed S. Hamza محمد صلاب حمزة AU - Hayder Raheem Kareem حيدر رحيم كريم PY - 2013 VL - 17 IS - 6 SP - 78 EP - 86 JO - Journal of Engineering and Sustainable Development (JEASD) مجلة الهندسة والتنمية المستدامة SN - 25200917 25200925 AB - Experimental work had been done to demonstrate the effect of nanocarbon black particles (N220) contents on the mechanical and tribological behavior of unsaturated polyester nanocomposite prepared via ultrasonic wave dispersion method. The results showed that the mechanical and tribological behavior was enhanced when the nanocarbon black particles content was increased up to 2%wt. and then decreased after that. The improvements in compressive strength and flexural strength are (16.13% at 2%wt. and 25.2% at 1%wt.), respectively, While The improvements in the hardness and wear resistance are (14.65% and 25.76% ) at 2%wt. , respectively.

تم أجراء دراسة تجريبية لبيان تاثير كمية حبيبات الكاربون الاسود النانوي (N220) في السلوك الميكانيكي و الترايبولوجي لراتنج البوليستر المدعم بها بطريقة التشتت بالموجات فوق الصوتية .بينت النتائج العملية ان السلوك الميكانيكي والترابيولجي للمتراكب النانوي يتحسن عند زيادة النسبة المئوية إلى حد 2% من الكاربون الأسود النانوني وبعد ذلك ينخفض, حيث ان نسبة التحسن لمقاومة الانضغاط ومقاومة الانحناء هي (16.13% عند النسبة المئوية 2% و25,2% عند النسبة المئوية 1% ) على التوالي, بينما مقاومة الصلادة والبلى تحسنت بنسبة (14,65% و25,76% ) عند النسبة المئوية (2%) على التوالي . الكلمات الدالة : مقاومة الانضغاط , مقومة الانحناء , مقاومة الصلادة , مقاومة البلى ,الكاربون الأسود النانوي والبوليستر الغير مشبع . ER -