TY - JOUR ID - TI - Structural and microhardness studies of Al-Ni-Cr alloy ingots AU - Khalid H. Abass AU - Foaad SH. Hashim PY - 2014 VL - 22 IS - 4 SP - 1414 EP - 1420 JO - Journal of University of Babylon مجلة جامعة بابل SN - 19920652 23128135 AB - Ingots of Al and Al-Ni-Cr (contains 0.25,0.5,0.99,1.98 at.% Ni-Cr) alloys were prepared by melting together wire aluminium, powder nickel and very small pieces of chromium in an electric furnace at 800 oC under an argon atmosphere. XRD analysis after exposed the alloys to annealing at 560 oC for 1300 hr showed the emergence and growth of three binary phases: Al3Ni(Orthorhombic, a=6.598Ǻ, b=7.352 Ǻ, c=4.802 Ǻ), Cr9Al17(Rhombohedral, a=12.910, c=15.677 Ǻ), and Ni2Cr3(Tetragonal, a=8.82 Ǻ, c=4.58 Ǻ) in addition to unknown phases. The crystallite size decrease with increasing Ni-Cr contents exception the ratio 1.98 at.%. The results refer to rising of microhardness three times when raised the alloy density 0.1 g/cm3. Keywords: Al-Ni-Cr alloy, crystallite size, microhardness

مسبوكة Al و Al-Ni-Cr (المحتوية على نسب مختلفة من Ni-Cr بالمقدار 0.25، 0.5، 0.99، 1.98) المحضرة باذابة اسلاك من الالمنيوم مع مسحوق النيكل وقطع صغيرة جداً من الكروم في فرن كهربائي بدرجة حرارة مقدارها 800 oC تحت فراغ من الاركون. بعد المعاملة الحرارية للنماذج المحضرة بدرجة 560 oC لفترة 1300 hr، يبين حيود الاشعة السينية ظهور ونمو ثلاثة اطوار ثنائية: Al3Ni(معيني، a=6.598، b=7.352، c=4.802)، Cr9Al17(موشوري سداسي،( c=15.677 ,a=12.910 و Ni2Cr3( رباعي الزوايا،(c=4.58 ,a=8.82 اضافةً الى اطوار غير معروفة. الحجم الحبيبي يقل بزيادة محتوى Ni-Cr في السبيكة باستثناء النسبة 1.98at%. النتائج تشير الى زيادة الصلادة الدقيقة ثلاثة اضعاف بزيادة الكثافة بمقدار 0.1 g/cm3. ER -