TY - JOUR ID - TI - Effect of sintering time on Bi1.6Pb0.4Sr1.8Ba0.2Ca2Cu3O10+ compound quenched in air and liquid nitrogen تاثير زمن التلبيد على المركب Bi1.6Pb0.4Sr1.8Ba0.2Ca2Cu3O10+ المبرد فجائيا بالهواء والنتروجين السائل AU - Hassan A.Thabit حسن عبدالله ثابت AU - Bushra A. Aljurani بشرى عبد الوهاب الجوراني AU - Ghazala Y. Hermiz غزالة يلدا هرمز PY - 2014 VL - 11 IS - 2 عدد خاص بالمؤتمر النسوي الثاني SP - 713 EP - 717 JO - Baghdad Science Journal مجلة بغداد للعلوم SN - 20788665 24117986 AB - High temperature superconductor with nominal composition Bi1.6Pb0.4Sr1.8Ba0.2Ca2 Cu3O10+ was prepared by solid state reaction method. Two sets of samples have been prepared .The first one was quenched in air; the second set was quenched in liquid nitrogen. X-ray diffraction analyses showed an orthorhombic structure with two phases, high –Tc phase (2223) and low-Tc phase (2212) in addition to that impure phase was found. It has been observed that quenched in air samples display a sharp superconducting transition and a higher-Tc phase than that of the quenched in liquid nitrogen samples.

تم تحضير المركب Bi1.6Pb0.4Sr1.8Ba0.2Ca2Cu3O10+ الفائق التوصيل بطريقة تفاعل الحالة الصلبة.حضرت مجموعتين من العينات ودرست ظروف التبريد واختلاف زمن التلبيد حيث تم تبريد عينات المجموعة الاولى في الهواء بينما بردت عينات المجموعة الثانية في سائل النيتروجينبينت تحليلات حيود الأشعة السينية ان جميع العينات لها تركيب المعيني القائم وبطورين، الطور الفائق التوصيل العالي (2333) والطور الفائق التوصيل الواطىء (2212) مع وجود طور الشوائب. .ولوحظ ايضا ان العينات المبردة سريعاً بالهواء اظهرت انتقال حاد من حالة التوصيل الاعتيادي الى حالة التوصيل الفائق وبدرجة حرارة حرجة اعلى من العينات المبردة في سائل النيتروجين. ER -