@Article{, title={Superplastic Behavior of AZ31B Magnesium Alloy Processed by Equal Channel Angular Pressing (ECAP) سلوك اللدونة الفائقة لسبيكة المغنيسيوم من نوع AZ31B المشكلة بواسطة قلب بثق متساوي المقطع}, author={Ziad Tariq Madhloom and Azal R. Ismail}, journal={Engineering and Technology Journal مجلة الهندسة والتكنولوجيا}, volume={32}, number={8 Part (A) Engineering}, pages={1958-1970}, year={2014}, abstract={AZ31B magnesium alloy with initial grain size of 11.2 µm was grain refined using Equal Channel Angular Pressing (ECAP) the alloy was ECAP-processed up to 5-times at 473 K. As a result, the grains are refined to 2.1 µm after three ECAP passes, the elongation was increased to 84 % at 473 K and strain rate of 1×10-4 s-1 after ECAP up to 5-passes,. Large fracture elongations of 261% are obtained at 623 K and strain rate 2.45×10-4 s-1 for specimen made from 3 ECAR passes compared to 183% for the as received material. Also the superplastic properties of the ECAP-processed specimens were investigated at 623 K and the strain rate ranges from 2.45×10-4 s-1 to 1.2×10-3 s-1. The strain rate sensitivity were determined to be 0.33

تم استخدام قالب بثق متساوي المقطعECAP وذلك لتنعيم سبيكة المغنيسيوم من نوع AZ31B والتي تمتلك بنية مجهرية بحدود 11.2 مايكرو متر , تم استخدام تقنية ECAP لهذه السبكية لخمسة مرات و بدرجة حرارة 423 ° كلفن وكنتيجة لذلك تم تنعيم البنية المجهرية الى 2.1 ميكرو متر , و كذلك اصبحت الاستطالة 84% في درجة حرترة 423°كلفن و معدل انفعال 1×10-4s-1 و بعد خمسة تمريرات في قالب ECAP , ايضا تم فحص اللدونة الفائق superplastic test حيث اعطت السبيكة استطالة بحدود 261% في درجة حرارة 623° كلفن و معدل انفعال 2.45×10-4s-1 لعينات مصنوعة من ثلاث كبسات في قالب ECAP مقارنة مع183% استطالة للمادة بدون اجراء عملية ECAP .} }