Structural and Optical Properties of SnO2:MgO Thin Films Preparing by Pulse Laser Deposition Technique at 423K

الخصائص التركيبية والبصرية لأغشية SNO2 : MgO المحضرة بتقنية ترسيب الليزر النبضي عند 423 K

BatoolGabarAbead --- MajedH.Dwech --- KadhemA.Aadim

journal of kerbala university مجلة جامعة كربلاء
ISSN: 18130410 Year: 2015 Volume: 13 Issue: 3 Pages: 293-302
Publisher: Kerbala University جامعة كربلاء

Abstract

Transparent conducting magnesium oxide-doped tin oxide(SnO2:MgO) films have been deposited on glass substrates by pulsed laser deposition.structural, and optical, properties of these films have beeninvestigated. The films crystallize in a tetragonal structure and X-ray diffractionmeasurements have shown that the polycrystalline SnO2 films .The optical properties of the SnO2:MgO films have been investigated as a function of MgO-doping level and substrate deposition temperature ,average optical transmittance of( 82%) in the visible range, and optical band-gap of (3.45eV) were obtained for (423K) SnO2:MgO films.

تم في هذا البحث دراسة ترسيب اغشيه اوكسيد القصدير المطعمهباوكسيد المغنسيومعلى قواعد من الزجاج باستخدام تقنية الليزر النبضي, الخصائص التركيبيهوالبصريه تم دراستها اذ اوضحت النتائج التركيبيه ان الاغشيهالمحضره متعددة التبلوروذات تركيب رباعي الزوايا اما القياسات البصريه فقد درست النفاذيهالبصريه وتجاوزت حوالي 82% من المنطقهالمرئيه وقيمة فجوة الطاقة التي حصلت عند درجة حرارة23 4 كلفن بلغت(3.45) الكترون- فولت